  Chemically-reduced graphene-oxide-supported gold nanoparticles are considered
here as catalytic materials for the reduction of oxygen in alkaline medium.
Gold nanoparticles are prepared by the chemical reduction method, in which the
NaBH4-prereduced Keggin-type phosphomolybdate heteropolyblue acts as the
reducing agent for the precursor (HAuCl4). Polyoxmetallate (PMo12O403-) capping
ligands stabilize gold nanoparticle deposits, facilitate their dispersion and
attachment to carbon supports. Indeed, it is apparent from the independent
diagnostic voltammetric experiments (in 0.5 mol dm-3 H2SO4) that
heteropolymolybdates form readily stable adsorbates on nanostructures of both
gold and carbon (reduced graphene oxide and Vulcan). It is reasonable to expect
that the polyoxometallate-assisted nucleation of gold has occurred in the
proximity of oxygenated defects existing on carbon substrates. Under conditions
of electrochemical diagnostic experiments (performed in 0.1 mol dm-3 KOH): (i)
the phosphomolybdate adsorbates are removed from the interface as they undergo
dissolution in alkaline medium; and (ii) the Au nanoparticles (Au loading, 30
{\mu}g cm-2) remain well-dispersed on the carbon as evident from transmission
electron microscopy. High electrocatalytic activity of the reduced-graphene
oxide-supported Au nanoparticles toward reduction of oxygen in alkaline medium
is demonstrated using cyclic and rotating ring-disk voltammetric experiments.
Among important issues are possible activating interactions between gold and
the support, as well as presence of structural defects existing on poorly
organized graphitic structure of reduced graphene oxide (as evident from Raman
spectroscopy).