  A high-strength dual alpha+beta phase titanium alloy Ti-6Al-4V is utilized as
a material for beam windows in several accelerator target facilities. However,
relatively little is known about how material properties of this alloy are
affected by high-intensity proton beam irradiation. With plans to upgrade
neutrino facilities at J-PARC and Fermilab to over 1 MW beam power, the
radiation damage in the window material will reach a few displacements per atom
(dpa) per year, significantly above the ~0.3 dpa level of existing data. The
RaDIATE collaboration has conducted a high intensity proton beam irradiation of
various target and window material specimens at BLIP facility, including a
variety of titanium alloys. Post-Irradiation Examination of the specimens in
the 1st capsule, irradiated at up to 0.25 dpa, is in progress. Tensile tests in
a hot cell at PNNL exhibited a clear signature of radiation hardening and loss
of ductility for Ti-6Al-4V, while Ti-3Al-2.5V, with less beta phase, exhibited
less severe hardening. Microstructural investigations will follow to study the
cause of the difference in tensile behavior between these alloys. High-cycle
fatigue (HCF) performance is critical to the lifetime estimation of beam
windows exposed to a periodic thermal stress from a pulsed proton beam. The 1st
HCF data on irradiated titanium alloys are to be obtained by a conventional
bend fatigue test at Fermilab and by an ultrasonic mesoscale fatigue test at
Culham Laboratory. Specimens in the 2nd capsule, irradiated at up to ~1 dpa,
cover typical titanium alloy grades, including possible radiation-resistant
candidates. These systematic studies on the effects of radiation damage of
titanium alloys are intended to enable us to predict realistic lifetimes of
current beam windows made of Ti-6Al-4V and to extend the lifetime by choosing a
more radiation and thermal shock tolerant alloy.