  Layers obtained by drying a colloidal dispersion of silica spheres are found
to be a good benchmark to test the elastic behaviour of porous media, in the
challenging case of high porosities and nano-sized microstructures. Classically
used for these systems, Kendall's approach explicitely considers the effect of
surface adhesive forces onto the contact area between the particles. This
approach provides the Young's modulus using a single adjustable parameter (the
adhesion energy) but provides no further information on the tensorial nature
and possible anisotropy of elasticity. On the other hand, homogenization
approaches (e.g. rule of mixtures, Eshelby, Mori-Tanaka and self-consistent
schemes), based on continuum mechanics and asymptotic analysis, provide the
stiffness tensor from the knowledge of the porosity and the elastic constants
of the beads. Herein, the self-consistent scheme accurately predicts both bulk
and shear moduli, with no adjustable parameter, provided the porosity is less
than 35%, for layers composed of particles as small as 15 nm in diameter.
Conversely, Kendall's approach is found to predict the Young's modulus over the
full porosity range. Moreover, the adhesion energy in Kendall's model has to be
adjusted to a value of the order of the fracture energy of the particle
material. This suggests that sintering during drying leads to the formation of
covalent siloxane bonds between the particles.