  Estimates of the exchange interaction parameter (J) between electronic
magnetic momenta residing in the d-shells of several divalent first row
transition metal ions, and those residing on the [TCNE]$^-$. anion-radicals
(TCNE = tetracyanoethylene) that are bonded to the metal ion are obtained by
the use of the EHCF method in the cluster approximation. The clusters geometry
was set according to that observed for Mn$^{II}$(TCNE)$_{1/2}$(I$_3$)$_{1/2}$
and M$^{II}$(TCNE)(C$_4$(CN)$_8$)$_{1/2}$ (M = Fe, Mn) with the [TCNE]$^{-.}$.
For the Mn$^{II}$(TCNE)$_{1/2}$(I$_3$)$_{1/2}$ two cluster types are
considered: one with the geometry corresponding to [TCNE]$^{-.}$ in the
two-dimensional layer, and another connecting the layers. For
M$^{II}$(TCNE)(C$_4$(CN)$_8$)$_{1/2}$ only the layer position of the
[TCNE]$^{-.}$ is considered. In all cases the LUMO (singly filled in the
material) is predominantly concentrated on the ethylenic C-C bond and is
antibonding. The J value for the Mn$^{II}$(TCNE)$_{1/2}$(I$_3$)$_{1/2}$ layer
is at least as twice as strong as one for the similar geometry for
M$^{II}$(TCNE)(C$_4$(CN)$_8$)$_{1/2}$. The correct order of magnitude of the
calculated exchange parameters, as compared with those extracted from
experimentsindicates the general validity of this approach. However, the direct
comparison of these J values with the critical temperatures is not possible
since these latter heavily depend on details of the interlayer coupling not
available through the EHCF procedure. In order to get more information on the
geometry dependence of the exchange parameters, the dependence on the tilt
angle of the TCNE with respect to the plane formed by the metal ions and four
equatorial NCMe groups was investigated. In all cases, a remarkably strong
dependence, having different trends depending on the number of electrons in the
d-shells of respective transition metal ions was observed.