  Lithium iron phosphate (LixFePO4), a cathode material used in rechargeable
Li-ion batteries, phase separates upon de/lithiation under equilibrium. The
interfacial structure and chemistry within these cathode materials affects
Li-ion transport, and therefore battery performance. Correlative imaging of
LixFePO4 was performed using four-dimensional scanning transmission electron
microscopy (4D-STEM), scanning transmission X-ray microscopy (STXM), and X-ray
ptychography in order to analyze the local structure and chemistry of the same
particle set. Over 50,000 diffraction patterns from 10 particles provided
measurements of both structure and chemistry at a nanoscale spatial resolution
(16.6-49.5 nm) over wide (several micron) fields-of-view with statistical
robustness.LixFePO4 particles at varying stages of delithiation were measured
to examine the evolution of structure and chemistry as a function of
delithiation. In lithiated and delithiated particles, local variations were
observed in the degree of lithiation even while local lattice structures
remained comparatively constant, and calculation of linear coefficients of
chemical expansion suggest pinning of the lattice structures in these
populations. Partially delithiated particles displayed broadly core-shell-like
structures, however, with highly variable behavior both locally and per
individual particle that exhibited distinctive intermediate regions at the
interface between phases, and pockets within the lithiated core that correspond
to FePO4 in structure and chemistry.The results provide insight into the
LixFePO4 system, subtleties in the scope and applicability of Vegards law
(linear lattice parameter-composition behavior) under local versus global
measurements, and demonstrate a powerful new combination of experimental and
analytical modalities for bridging the crucial gap between local and
statistical characterization.