  Cu2-xTe nanocubes were used as starting seeds to access metal telluride
nanocrystals by cation exchanges at room temperature. The coordination number
of the entering cations was found to play an important role in dictating the
reaction pathways. The exchanges with tetrahedrally coordinated cations (i.e.
with coordination number 4), such as Cd2+ or Hg2+, yielded monocrystalline CdTe
or HgTe nanocrystals with Cu2-xTe/CdTe or Cu2-xTe/HgTe Janus-like
heterostructures as intermediates. The formation of Janus-like architectures
was attributed to the high diffusion rate of the relatively small tetrahedrally
coordinated cations, which could rapidly diffuse in the Cu2-xTe NCs and
nucleate the CdTe (or HgTe) phase in a preferred region of the host structure.
Also, with both Cd2+ and Hg2+ ions the exchange led to wurtzite CdTe and HgTe
phases rather than the more stable zinc-blende ones, indicating that the anion
framework of the starting Cu2- xTe particles could be more easily deformed to
match the anion framework of the metastable wurtzite structures. As hexagonal
HgTe had never been reported to date, this represents another case of
metastable new phases that can only be accessed by cation exchange. On the
other hand, the exchanges involving octahedrally coordinated ions (i.e. with
coordination number 6), such as Pb2+ or Sn2+, yielded rock-salt polycrystalline
PbTe or SnTe nanocrystals with Cu2-xTe@PbTe or Cu2-xTe@SnTe core@shell
architectures at the early stages of the exchange process. In this case, the
octahedrally coordinated ions are probably too large to diffuse easily through
the Cu2-xTe structure: their limited diffusion rate restricts their initial
reaction to the surface of the nanocrystals, where cation exchange is initiated
unselectively, leading to core@shell architectures.