  Manganese tricyanomethanide, Mn[C(CN)3]2, consists of two interpenetrating
three-dimensional rutile-like networks. In each network, the tridentate C(CN)3-
anion gives rise to superexchange interactions between the Mn2+ ions (S=5/2)
that can be mapped onto the "row model" for partially frustrated triangular
magnets. We present heat capacity measurements that reveal a phase transition
at T_N = 1.18K, indicative of magnetic ordering. The zero-field magnetically
ordered structure was solved from neutron powder diffraction data taken between
0.04 and 1.2 K. It consists of an incommensurate spiral with a temperature
independent propagation vector Q=(2Q 0 0)=(+/-0.622 0 0), where different signs
relate to the two different networks. This corresponds to (+/-0.311 +/-0.311 0)
in a quasi-hexagonal representation. The ordered moment mu=3.3mu_B is about 2/3
of the full Mn2+ moment. From the values of T_N and Q, the exchange parameters
J/k = 0.15 K and J'/J = 0.749 are estimated. The magnetic-field dependence of
the intensity of the <2Q 0 0> Bragg reflection, measured for external fields
H||Q, indicates the presence of three different magnetic phases. We associate
them with the incommensurate spiral (H < 13.5 kOe), an intermediate phase (13.5
kOe < H < 16 kOe), and the "2-1" spin-flop like magnetic structure (H > 16 kOe)
proposed for related compounds. For increasing fields, Q continuously
approaches the value 1/3, corresponding to the commensurate magnetic structure
of the fully frustrated triangular lattice. This value is reached at H_c = 19
kOe. At this point, the field-dependence reverses and Q adopts a value of 0.327
at 26 kOe, the highest field applied in the experiment. Except for H_c, the
magnetic ordering is incommensurate in all three magnetic phases of
Mn[C(CN)3]2.