  The transport coefficients of dense polymeric fluids are approximately
calculated from the microscopic intermolecular forces. The following finite
molecular weight effects are discussed within the Polymer-Mode-Coupling theory
(PMC) and compared to the corresponding reptation/ tube ideas: constraint
release mechanism, spatial inhomogeneity of the entanglement constraints, and
tracer polymer shape fluctuations. The entanglement corrections to the single
polymer Rouse dynamics are shown to depend on molecular weight via the ratio
N/N_e, where the entanglement degree of polymerization, N_e, can be measured
from the plateau shear modulus. Two microscopically defined non-universal
parameters, an entanglement strength 1/alpha and a length scale ratio, delta=
xi_rho/b, where xi_rho and b are the density screening and entanglement length
respectively, are shown to determine the reduction of the entanglement effects
relative to the reptation- -like asymptotes of PMC theory. Large finite size
effects are predicted for reduced degrees of polymerization up to N/N_e\le10^3.
Effective power law variations for intermediate N/N_e of the viscosity, eta\sim
N^x, and the diffusion constant, D\sim N^{-y}, can be explained with exponents
significantly exceeding the asymptotic, reptation-like values, x\ge 3 and
y\ge2, respectively. Extensions of the theory to treat tracer dielectric
relaxation, and polymer transport in gels and other amorphous systems, are also
presented.