  We generalize and apply a microscopic force-level statistical mechanical
theory of the activated dynamics of dilute spherical penetrants in
glass-forming liquids to study the influence of permanent crosslinking in
polymer networks on the penetrant relaxation time and diffusivity over a wide
range of temperature and crosslink density. Calculations are performed for
model parameters relevant to recent experimental studies of an nm-sized organic
molecule diffusing in crosslinked PnBA networks. The theory predicts the
penetrant alpha relaxation time increases exponentially with the crosslink
fraction ($f_n$) dependent glass transition temperature, $T_g$, which grows
roughly linearly with the square root of $f_n$. Moreover, $T_g$ is also found
to be proportional to a geometric confinement parameter defined as the ratio of
the penetrant diameter to the mean network mesh size. The decoupling ratio of
the penetrant to polymer Kuhn segment alpha relaxation times displays a complex
non-monotonic dependence on crosslink density and temperature that can be well
collapsed based on the variable $T_g(f_n)/T$. The microscopic mechanism for
activated penetrant relaxation is elucidated and a model for the penetrant
diffusion constant that combines activated segmental dynamics and entropic mesh
confinement is proposed which results in a significantly stronger suppression
of mass transport with degree of effective supercooling than predicted for the
penetrant alpha time. This behavior corresponds to a new polymer network-based
type of decoupling of diffusion and relaxation. In contrast to the diffusion of
larger nanoparticles in high temperature rubbery networks, our analysis in the
deeply supercooled regime suggests that for the penetrants studied the mesh
confinement effects are of secondary importance relative to the consequences of
crosslink-induced slowing down of glassy activated relaxation.