  The OH-terminated self-assembled monolayers, as protein-resistant surfaces,
have significant potential in biocompatible implant devices, which can avoid or
reduce adverse reactions caused by protein adhesion to biomaterial surfaces,
such as thrombosis, immune response and inflammation. Here, molecular dynamics
simulations were performed to evaluate the degree of protein adsorption on the
self-assembled monolayer terminated with two hydrophilic OH groups ((OH)2-SAM)
at the packing densities ({\Sigma}) of 4.5 nm-2 and 6.5 nm-2, respectively. The
results show that the (OH)2-SAM itself can significantly improve the
performance of its resistance to protein adsorption. This is attributed to the
structure of the (OH)2-SAM itself, i.e., the formation of a nearly perfect
hexagonal-ice-like hydrogen bond structure in the OH matrix of the (OH)2-SAM at
{\Sigma} = 4.5 nm-2, which sharply reduces the number of hydrogen bonds (i.e.,
0.9) formed between the hydrophobic (OH)2-SAM surface and protein. While for
{\Sigma} = 6.5 nm-2, the hydrophilic (OH)2-SAM surface can provide more
hydrogen bonding sites to form hydrogen bonds (i.e., 7.3) with protein. The
number of hydrogen bonds formed between the (OH)2-SAM and protein at {\Sigma} =
6.5 nm-2 is ~8 times higher than that at {\Sigma} = 4.5 nm-2, reflecting the
excellent resistance to protein adsorption exhibited by the structure of
(OH)2-SAM itself at {\Sigma} = 4.5 nm-2. Compared with traditionally physical
barrier effect formed by a large number of hydrogen bonds between the (OH)2-SAM
and water above at {\Sigma} = 6.5 nm-2, the structure of the (OH)2-SAM itself
at {\Sigma} = 4.5 nm-2 proposed in this study significantly improves resistance
to protein adsorption, which provides new insights into the mechanism of
resistance to protein adsorption on the (OH)2-SAM.