  Chemical nature of point defects, their segregation, cluster or complex
formation in ZnO is an important area of investigation. In this report, 1.2 MeV
Ar ion beam is used to incorporate defects in granular ZnO. Evolution of
defective state with irradiation fluence 1 x 10^14 and 1 x 10^16 ions/cm2 has
been monitored using XPS, PL and Raman spectroscopic study. XPS study shows
presence of oxygen vacancies (VO) in the Ar ion irradiated ZnO. Zn(LMM) Auger
spectra clearly identifies transition involving metallic zinc in the irradiated
samples. Intense PL emission from IZn related shallow donor bound excitons
(DBX) is visible in the 10 K spectra for all samples. Although overall PL is
largely reduced with irradiation disorder, DBX intensity is increased for the
highest fluence irradiated sample. Raman study indicates damage in both zinc
and oxygen sub-lattice by energetic ion beam. Representative Raman modes from
defect complexes involving VO, IZn and IO are visible after irradiation with
intermediate fluence. Further increase of fluence shows, to some extent, a
homogenization of disorder. Huge reduction of resistance is also noted for this
sample. Certainly, high irradiation fluence induces a qualitative modification
of the conventional (and highly resistive) grain boundary (GB) structure of
granular ZnO. Low resistive path, involving IZn related shallow donors, across
the GB can be presumed to explain resistance reduction. Open volumes (VZn and
VO) agglomerate more and more with increasing irradiation fluence and finally
get transformed to voids. Results as a whole have been elucidated with a model
which emphasizes possible evolution of new defect microstructure that is
distinctively different from the GB related disorder. Based on the model,
qualitative explanations of commonly observed radiation hardness, colouration
and ferromagnetism in disordered ZnO have been put forward.