  Demand for artificial body implants has been on the rise over the years.
However, wear and bacterial infection are identified as two major reasons that
can lead to inflammation and implant failure. In this communication, the
advantages of pulsed laser deposited zirconia thin film on Ti6Al4V bio-alloy at
room temperature and at an elevated substrate temperature are discussed wherein
a comparison of the change in surface roughness, wettability, surface free
energy, tribological and antibacterial properties of uncoated and zirconia
coated Ti6Al4V samples is presented. The results of tribological analysis
carried out using a standard ball-on-disc tribometer at different loads (2N, 5N
and 7N) exhibited advantageous effects of zirconia coating on Ti6Al4V.
Prominently, the sample coated at 200 C substrate temperature maintained very
low coefficient of friction up to hundreds of sliding cycles and showed a
notable reduction in the wear rate by 49% at 5N load. The in vitro bacterial
retention test showed a clear inhibition in growth of Staphylococcus aureus and
Klebsiella pneumonia bacteria on the surface of the coated samples indicating
the possibility of prevention of biofilm formation. More than 50% reduction in
density of Staphylococcus aureus was observed on coated sample in comparison to
pristine Ti6Al4V and this can be attributed to reduction in surface energy of
the sample after coating. Additionally, the observation of a larger number of
decimated bacteria on coated samples by fluorescence microscopy revealed
superior antibacterial properties of zirconia coating. The novelty of this work
is the use of pulsed laser deposition technique for zirconia coating which
dearly improves tribological and antibacterial properties of Ti6Al4V
simultaneously; this shows prospects of increasing durability of artificial
implant in the human body.