  In the pulp and paper industry, about 5 Mt/y chemithermomechanical pulp
(CTMP) are produced globally from softwood chips for production of carton board
grades. For tailor making CTMP for this purpose, wood chips are impregnated
with aqueous sodium sulphite for sulphonation of the wood lignin. When lignin
is sulphonated, the defibration of wood into pulp becomes more selective,
resulting in enhanced pulp properties. On a microscopic fibre scale, however,
one could strongly assume that the sulphonation of the wood structure is very
uneven due to its macroscale size of wood chips. If this is the case and the
sulphonation could be done significantly more evenly, the CTMP process could be
more efficient and produce pulp even better suited for carton boards.
Therefore, the present study aimed to develop a technique based on X-ray
fluorescence microscopy imaging (uXRF) for quantifying the sulphur distribution
on CTMP wood fibres.
  The feasibility of uXRF imaging for sulphur homogeneity measurements in wood
fibres needs investigation. Clarification of which spatial and spectral
resolution that allows visualization of sulphur impregnation into single wood
fibres is needed. Measurements of single fibre imaging were carried out at the
APS synchrotron facility. With a synchrotron beam using 1 um scanning step,
images of elemental mapping are acquired from CTMP samples diluted with
non-sulphonated pulp under specified conditions. Since the measurements show
significant differ-ences between sulphonated and non-sulphonated fibres, and a
significant peak concentration in the shell of the sulphonated fibres, the
proposed technique is found to be feasible. The required spatial resolution of
the uXRF imaging for an on-site CTMP sulphur homogeneity measurement setup is
about 15 um, and the homogeneity measured along the fibre shells is suggested
to be used as the CTMP sulphonation measurement parameter.