  It is difficult to predict material behavior under decades long irradiation
regimes. Machine and deep learning can be very important tools that can help
predict resulting material properties. These tools require strong and robust
models that can carefully reproduce the microstructural evolution against
experiments so researchers can understand the material processes and to
validate the model for future use with other materials. Thus, a newly developed
Kinetic Monte Carlo (KMC) model was constructed to investigate the
precipitation behavior of Y-Ti-O oxides along grain boundaries in
nanostructured ferritic alloys (NFA) and the oxide response to neutron
irradiation. The level of radiation damage simulated reached the long dpa range
required for reactor components. Simulations were conducted to investigate the
influence of temperature as well as the influence of grain boundary sinks on
the resulting oxide characteristics of a 12YWT-like alloy during heat
treatments at 1023K - 1223K. There is good agreement of the oxide
characteristics from simulation with literature values and the influence of the
grain boundary on precipitation is slight. The same oxide configuration and
positions were input into a new simulation and placed under simulated neutron
irradiation to a total accumulated dose of 8 dpa at temperatures, 673K - 873K,
and at dose rates of 10^-3, 10^-4, and 10^-5. The expected inverse relationship
of oxide size with dose rate was observed. A long-term irradiation simulation
at 873K and 10^-3 dpa/s was taken to 66 dpa and it was found that the oxides in
the vicinity of the grain boundary were more susceptible to dissolution.
Additionally, irradiation simulations of a 14YWT-like alloy were conducted to
replicate findings from neutron irradiation experiments. The larger oxides in
the 14YWT-like alloy did not dissolve and showed the same stability as in the
experiments.