  Magnon diffuse scattering (MDS) signals could be studied with high spatial
resolution in scanning transmission electron microscopy (STEM), thanks to
recent technological progress in electron energy loss spectroscopy. However,
detecting MDS signals in STEM is challenging due to their overlap with stronger
thermal diffuse scattering (TDS) signals. In bcc Fe at 300 K, MDS signals
greater than or comparable to TDS signals occur under the central Bragg disk,
into a currently inaccesible energy-loss region. Therefore, to detect MDS in
STEM, it is necessary to find conditions in which TDS and MDS signals can be
separated. Temperature may be a key factor due to the distinct thermal
signatures of magnon and phonon signals. In this work, we present a study on
the effects of temperature on MDS and TDS in bcc Fe -- considering a detector
outside the central Bragg disk and a fixed convergent electron probe -- using
the frozen phonon and frozen magnon multislice methods. Our study reveals that
neglecting the effects of atomic vibrations causes the MDS signal to grow
approximately linearly up to the Curie temperature of Fe, after which it
exhibits less variation. The MDS signal displays an alternating behavior due to
dynamical diffraction, instead of increasing monotonically as a function of
thickness. Including the effects of atomic vibrations through a complex atomic
electrostatic potential causes the linear growth of the MDS signal to change to
a non-linear behavior that exhibits a predominant peak for a sample of
thickness 16.072 nm at 1100 K. In contrast, the TDS signal grows more linearly
than the MDS signal but still exhibits appreciable dynamical diffraction
effects. An analysis of the signal-to-noise ratio (SNR) shows that the MDS
signal can be a statistically significant contribution to the total scattering
intensity under realizable measurement conditions and acquisition times.