  The free standing solid polymer nanocomposite films has been prepared through
standard solution cast technique. The improvement in structural,
microstructural and electrochemical properties has been observed on the
dispersion of nanofiller in polymer salt complex. X Ray diffraction studies
clearly reflect the formation of complex formation as no corresponding salt
peak appeared in the diffractograms. The FTIR analysis suggested a clear and
convincing evidence of polymer ion, ion ion and polymer ion nanofiller
interaction. The highest ionic conductivity of the prepared solid polymer
electrolyte films is 5x10-5 S cm-1 for 7 wt. TiO2. The Linear Sweep Voltammetry
provide the electrochemical stability window of the prepared solid polymer
electrolyte films, which is of the order of 3.5 V. The ion transference number
has been estimated, tion is 0.99 through dc polarization technique. Dielectric
spectroscopic studies were performed to understand the ion transport process in
polymer electrolytes. All solid polymer electrolyte possesses good thermal
stability up to 300C. DSC analysis confirms the decrease of melting temperature
and signal of glass transition temperature with addition of nanofiller which
indicates the decrease of crystallinity of polymer matrix. An absolute
correlation between diffusion coefficient, ion mobility, number density, double
layer capacitance, glass transition temperature, melting temperature, free ion
area and conductivity has been observed. A convincing model to study the role
of nanofiller in polymer salt complex has been proposed which supports the
experimental findings. The prepared polymer electrolyte system with significant
ionic conductivity, high ionic transference number, good thermal, voltage
stability could be suggested as a potential candidate as electrolyte cum
separator for fabrication of rechargeable lithium-ion battery system.