  LPBF of Al alloys is associated with numerous challenges when compared to
other commonly used alloys due to their higher reflectivity and thermal
conductivity. In this work, processing diagrams, temperature prediction models,
XCT, and metallography are used for establishing criteria in process parameter
optimization of high reflectivity Al alloys based on AlSi$_{10}$Mg response in
using 57 different process parameter combinations - 21 using a focused Gaussian
laser beam and 36 using divergent beams. For LPBF systems with focused beam
diameters <100 {\mu}m, divergent beams obtained by defocusing to a position
above the LPBF build plate primarily lead to conduction mode melt pools, while
a focused beam leads to transition and keyhole mode melt pools. Conduction mode
melting helps in avoiding keyhole mode defects, resulting in parts with
densities >99.98%. Additionally, an analytical model-guided selection of laser
power and velocity settings for a focused beam help in stabilizing melt pool
and spatter dynamics in the transition melting mode thereby enabling a
potential to obtain density values close to conduction mode densities
(~99.98%). A dimensionless keyhole number (Ke) was derived in this work to
identify distinct regions of conduction (Ke of 0-12), transition (Ke of 12-20),
and keyhole (Ke > 20) mode melting during LPBF of AlSi$_{10}$. A melt pool
aspect ratio (ratio of melt pool depth to width) of ~0.4 is observed to be the
threshold between conduction and transition/keyhole mode melt pools for
AlSi$_{10}$, different from the conventionally assumed 0.5. Lastly, inferred
laser absorptivity values (from experimental melt pools) of transition/keyhole
mode melt pools are observed to be >40% higher when compared to conduction mode
melt pools. This work demonstrates a dimensionless-process map method to obtain
near fully dense parts that can be generalized for LPBF of high reflectivity
alloys.