  In this work, the capability of primary, monocyte-derived dendritic cells
(DCs) to uptake iron oxide magnetic nanoparticles (MNPs) is assessed and a
strategy to induce selective cell death in these MNP-loaded DCs using external
alternating magnetic fields (AMFs) is reported. No significant decrease in the
cell viability of MNP-loaded DCs, compared to the control samples, was observed
after five days of culture. The amount of MNPs incorporated into the cytoplasm
was measured by magnetometry, which confirmed that 1 to 5 pg of the particles
were uploaded per cell. The intracellular distribution of these MNPs, assessed
by transmission electron microscopy, was found to be primarily inside the
endosomic structures. These cells were then subjected to an AMF for 30 min, and
the viability of the blank DCs (i.e., without MNPs), which were used as control
samples, remained essentially unaffected. However, a remarkable decrease of
viability from approximately 90% to 2-5% of DCs previously loaded with MNPs was
observed after the same 30 min exposure to an AMF. The same results were
obtained using MNPs having either positive (NH2+) or negative (COOH-) surface
functional groups. In spite of the massive cell death induced by application of
AMF to MNP-loaded DCs, the amount of incorporated magnetic particles did not
raise the temperature of the cell culture. Clear morphological changes at the
cell structure after magnetic field application were observed using scanning
electron microscopy. Therefore, local damage produced by the MNPs could be the
main mechanism for the selective cell death of MNP-loaded DCs under an AMF.
Based on the ability of these cells to evade the reticuloendothelial system,
these complexes combined with an AMF should be considered as a potentially
powerful tool for tumour therapy.