  This study has explored numerous physical properties of
CaPd$_3$Ti$_4$O$_{1}$2 (CPTO) and CaPd$_3$V$_4$O$_{12}$ (CPVO) quadruple
perovskites employing the density functional theory (DFT) method. The
mechanical permanence of these two compounds was observed by the Born stability
criteria as well. The band structure of CPTO reveals a 0.88 and 0.46 eV direct
narrow band gap while using GGA-mBJ and GGA-PBE potentials, respectively, which
is an indication of its fascinating semiconducting nature. The calculated
partial density of states indicates the strong hybridization between Pd-4d and
O-2p orbital electrons for CPTO, whereas Pd-4d and V-3d-O-2p for CPVO. The
study of the chemical bonding nature and electronic charge distribution graph
reveals the coexistence of covalent O-V/Pd bonds, ionic O-Ti/Ca bonds, as well
as metallic Ti/V-Ti/V bonding for both compounds. The Fermi surface of CPVO
ensures a kind of hole as well as electron faces simultaneously, indicating the
multifarious band characteristic. The prediction of the static real dielectric
function (optical property) of CPTO at zero energy implies its promising
dielectric nature. The photoconductivity and absorption coefficient of CPBO
display good qualitative compliance with the consequences of band structure
computations. The calculated thermodynamic properties manifest the
thermodynamical stability for CPBO, whereas phonon dispersions of CPVO exhibit
stable phonon dispersion in contrast to slightly unstable phonon dispersion of
CPTO. The predicted Debye temperature ($\theta_D$) has been utilized to
correlate its topical features including thermoelectric behaviors. The studied
thermoelectric transport properties of CPTO yielded the Seebeck coefficient
(186 V/K), power factor (11.9 Wcm$^{-1}$K$^{-2}$), and figure of merit (ZT)
value of about 0.8 at 800 K, indicating that this material could be a promising
candidate for thermoelectric applications.