  The surface coating of cathodes using insulator films has proven to be a
promising method for high-voltage cathode stabilization in Li-ion batteries.
However, there is still substantial uncertainty about how these films function,
specifically with regard to important coating design principles such as lithium
solubility and transport through the films. This study uses Density Functional
Theory to examine the diffusivity of interstitial lithium in crystalline
{\alpha}-$AlF_3$, {\alpha}-$Al_2O_3$, m-$ZrO_2$, c-MgO, and {\alpha}-quartz
$SiO_2$, which provide benchmark cases for further understanding of insulator
coatings in general. In addition, we propose an Ohmic electrolyte model to
predict resistivities and overpotential contributions under battery operating
conditions. For the crystalline materials considered we predict that Li+
diffuses quite slowly, with a migration barrier larger than 0.9 eV in all
crystalline materials except {\alpha}-quartz $SiO_2$, which is predicted to
have a migration barrier of 0.276 eV along <001>. These results suggest that
the stable crystalline forms of these insulator materials, except for oriented
{\alpha}-quartz $SiO_2$, are not practical for conformal cathode coatings.
Amorphous $Al_2O_3$ and $AlF_3$ have higher Li+ diffusivities than their
crystalline counterparts. Our predicted amorphous $Al_2O_3$ resistivity (1789
M{\Omega}m) is near the top of the range of fitted resistivities extracted from
previous experiments on nominal $Al_2O_3$ coatings (7.8 to 913 M{\Omega}m)
while our predicted amorphous $AlF_3$ resistivity (114 M{\Omega}m) is close to
the middle of the range. These comparisons support our framework for modeling
and understanding the impact on overpotential of conformal coatings in terms of
their fundamental thermodynamic and kinetic properties, and support that these
materials can provide practical conformal coatings in their amorphous form.