  A first-principles density functional method along with the direct solution
of linearized Boltzmann transport equations are employed to systematically
analyze the low-temperature thermal transport in crystalline GeTe. The
extensive thermal transport simulations, ranging from room temperature to
cryogenic temperatures, reveal the emergence of a phonon hydrodynamic regime in
GeTe at low temperature. The reduction of grain boundary scattering is found to
play a crucial role along with the divergent trend of umklapp and normal
scattering at low temperatures in accommodating the hydrodynamic regime.
Average scattering rates for normal, umklapp, and other resistive processes are
distinguished for a wide range (4-300 K) of temperatures and used for
identifying various phonon transport regimes. Therefore, the variations of
lattice thermal conductivity, phonon propagation length, and thermal
diffusivity with temperature, related to these transport regimes (ballistic,
hydrodynamic, and kinetic), have been thoroughly investigated. The modewise
decomposition of lattice thermal conductivity and the distinction of thermal
diffusivity according to different scattering processes reveal rich information
on the dominant phonon modes and phonon scattering processes in GeTe at low
temperature. Further, the kinetic-collective model is used to elucidate the
hydrodynamic behavior of phonon scattering through the relative study of
collective and kinetic contributions to the thermal transport properties. In
this context, the Knudsen number is estimated through the characteristic
nonlocal length and the grain size, which further quantifies the consistent
hydrodynamic behavior of phonon thermal transport for GeTe. Finally,
phonon-vacancy scattering for GeTe is realized, and vacancies are found
strongly to influence the hydrodynamic window while incorporating the other
resistive scattering mechanisms.