  Mn-Zn ferrite nanoparticles have been subject of increasing research due to
their desired properties for a wide range of applications. These properties
include nanometer particle size control, tunable magnetic properties and low
toxicity, providing these ferrites with the necessary requirements for cancer
treatment via magnetic hyperthermia. During this master thesis, powders of
Mn1-xZnxFe2O4 (x=0; 0.5; 0.8; 1) were synthesized via the sol-gel
autocombustion and hydrothermal methods, aiming to optimize their structural
and magnetic properties for further application in a ferrofluid. Samples were
characterized by XRD, SQUID, SEM, TEM and magnetic induction heating (MIH)
techniques. The XRD diffractograms of hydrothermally produced samples present
spinel crystal structure with high single-phase percentage (>88%). Rietveld
refinement and Williamson-Hall analysis reveal a decrease of lattice constant
and crystallite size with increase of Zn/Mn ratio. TEM images reveal narrow
particle size distributions and decrease of the mean particle size with
increase of Zn/Mn. SQUID results show that the increase of Zn results in a
decrease of saturation magnetization and remnant magnetization. More
noticeably, the M(T) curves present a shift in the samples magnetic ordering
temperature towards lower temperatures with the increase of Zn content, from
~556 to ~284 K. The MIH experiment also unveil a decrease in the heating rate
with the increase of Zn. Nanocrystals of Mn-Zn ferrite produced by hydrothermal
method present better crystallinity and magnetic properties than the sol-gel
auto-combustion samples. The hydrothermally synthesized samples revealed
dependence of its structural and magnetic properties with Mn/Zn ratio.The
magnetic ordering temperature of these ferrites can be used as a
self-controlled mechanism of heating, raising these ferrites to a class of
smart materials.