  A fundamental understanding of plasma-catalyst interactions is important for
understanding reaction mechanisms, optimizing the catalyst, and increasing the
efficiency of plasma-assisted catalytic process for ammonia (\ce{NH3})
synthesis. We report on the effect of the surface porosity of the catalyst
support on this reaction carried out in a coaxial dielectric barrier discharge
(DBD) plasma reactor. The discharge was created using a variable AC applied
voltage at room temperature and near atmospheric pressure (550 Torr). Two
catalyst supports were compared: porous silica (\ce{SiO2}) ceramic beads and
smooth, non-porous soda lime glass beads of almost equal diameter ($\sim$1.5
mm) were used. \ce{N2} conversion and the \ce{NH3} synthesis rate was increased
with increasing voltage for both supports, but the energy yield for \ce{NH3}
production increased for the \ce{SiO2} beads and decreased for the glass beads.
All three of these parameters were always higher when using the \ce{SiO2}
beads, which suggests that porosity can be a small advantage for plasma
assisted \ce{NH3} synthesis. Discharge and plasma properties were estimated
from Lissajous plots and using calculations with the BOLSIG+ software. The
effect of different catalyst supports on the physical properties of the
discharge was negligible. High resolution optical emission spectra (OES) were
used to explore the evolution of gas phase active species, \ce{N2+}, atomic N,
electronically excited \ce{N2}, and atomic H (H$_\alpha$, H$_\beta$), in the
plasma in the presence of both supports. The relative concentration of these
species was lower in the case of the porous \ce{SiO2} beads for all applied
voltages, which suggests that surface reactions are more significant than gas
phase reactions for the formation of \ce{NH3} in plasma assisted \ce{NH3}
synthesis.