  The process of localized cleaning of silver sulphide from the silver surface
has been investigated in this work. An artificial black encrustation was
generated on the silver surface and its laser cleaning was performed using an
excimer laser (KrF based) working at a wavelength of 248 nm and pulse width 25
ns. Laser process parameters i.e. laser fluence and number of pulses were used
to perform the experiment and after different optical, microstructural,
elemental, microhardness and surface topography analysis of the laser ablated
zone was performed. The parametric window selected for the excimer laser
cleaning were laser fluence (200-400 mJ/cm2), repetition rate 4 Hz and number
of pulses (60-300). It was observed that excimer laser is very effective in the
cleaning of black encrustation having 6 wt. % of sulphur from the surface
without any significant removal of the silver substrate. The fluence value of
260.48 mJ/cm2 was observed as above threshold value for removal of sulphide
from the encrusted surface while a fluence of 384.85 mJ/cm2 and 220 pulses
showed the maximum removal of sulphur encrustation (0.38 wt. % of sulphur
remaining). Formation of the peripheral rim was observed to occur above 280.17
mJ/cm2 of fluence value. The topography of the ablated surface showed a removal
of 5-10 um of the sulphide layer from the surface whereas the thickness of the
sulphide coating was around 8-10 um. Microhardness value showed a change of
microhardness of the silver surface from 75.12 HV0.5 (uncoated parent silver)
to 96.07 HV0.5 (centre of the ablated zone).Finally, it was concluded that
excimer laser cleaning is a novel method for localized removal of silver
sulphide encrustation from silver surface.