  In this study for the first time, polymeric nanofiltration membranes based on
polyethersulfone (PES) polymer were surface-modified by using a diamond-like
carbon (DLC) nanostructure coating layer. The effect of this coating on the
performance and anti-fouling properties of the membrane was investigated. The
surface-modified membranes significantly improved the salt separation and their
hydrophilicity was more than the control membrane after the reformation
process. The amount of salt separation increased from 64% to 98% due to the
decrease in the size of the holes on the surface. The absorption characteristic
of DLC nanostructure in contact with feed solution was reported as another
reason in this field. The contact angle (CA) of water also decreased due to the
improvement of hydrophilicity, which means the increase of hydrophilicity in
the above membranes. The amount of pure water flux passing through the
membranes increases from one side of the membrane surface to both sides with
the increase significantly of the coating level, so that its value reaches from
about 8L/m2h for the M0 membrane to 65L/m2h in the membrane containing M3. The
surface morphology of unmodified membranes changed from a rough state with an
average of 16nm in PES membranes to a smoother state in modified membranes with
an average of 9nm. The recovery rate of the flux and the total absorption rate
were obtained in complete agreement with the results obtained from the CA of
water and the amount of the calculated surface roughness parameter. The
increase in the flux recovery rate and the decrease in the fouling rate
indicated the successful improvement of the antifouling properties as a result
of the coating process. Based on the washing test, the prepared sample has good
stability against the number of washing cycles, which is a very important
advantage for practical applications.