  Polymers exposed to shear flow exhibit a rich tumbling dynamics. While rigid
rods rotate on Jeffery orbits, flexible polymers stretch and coil up during
tumbling. Theoretical results show that in both of these asymptotic regimes the
tumbling frequency f_c in a linear shear flow of strength \gamma scales as a
power law Wi^(2/3) in the Weissenberg number Wi=\gamma \tau, where \tau is a
characteristic time of the polymer's relaxational dynamics. For flexible
polymers these theoretical results are well confirmed by experimental single
molecule studies. However, for the intermediate semiflexible regime the
situation is less clear. Here we perform extensive Brownian dynamics
simulations to explore the tumbling dynamics of semiflexible polymers over a
broad range of shear strength and the polymer's persistence length l_p. We find
that the Weissenberg number alone does not suffice to fully characterize the
tumbling dynamics, and the classical scaling law breaks down. Instead, both the
polymer's stiffness and the shear rate are relevant control parameters. Based
on our Brownian dynamics simulations we postulate that in the parameter range
most relevant for cytoskeletal filaments there is a distinct scaling behavior
with f_c \tau*=Wi^(3/4) f_c (x) with Wi=\gamma \tau* and the scaling variable
x=(l_p/L)(Wi)^(-1/3); here \tau* is the time the polymer's center of mass
requires to diffuse its own contour length L. Comparing these results with
experimental data on F-actin we find that the Wi^(3/4) scaling law agrees
quantitatively significantly better with the data than the classical Wi^(2/3)
law. Finally, we extend our results to single ring polymers in shear flow, and
find similar results as for linear polymers with slightly different power laws.