  Electromagnetic theory predicts that the optimal value of the localized
plasmon resonance (LPR) wavelength for the maximal SERS enhancement factor (EF)
is half the sum of the laser and Raman wavelengths. For small Raman shifts, the
theoretical EF scales as the fourth power of the local field. However,
experimental data often disagree with these theoretical conclusions, leaving
the question of choosing the optimal plasmon resonance for the maximal SERS
signal unresolved. Here, we present experimental data for gold nanorods
(AuNRs), gold nanotriangles (AuNTs), and gold nanostars (AuNSTs). The LPR
wavelengths were tuned by chemical etching within 550-1050 nm at constant
number concentrations of the particles. The particles were functionalized with
Cy7.5 and NBT, and the dependence of the intensity at 940 cm-1 (Cy7.5) and 1343
cm-1 (NBT) on the LPR wavelength was examined for laser wavelengths of 633 nm
and 785 nm. The electromagnetic SERS EFs were calculated by averaging the
product of the local field intensities at the laser and Raman wavelengths over
the particle surface and their random orientations. The calculated SERS
plasmonic profiles were redshifted compared to the laser wavelength. For 785-nm
excitation, the calculated EFs were five to seven times higher than those for
633-nm excitation. With AuNR@Cy7.5 and AuNT@ Cy7.5, the experimental SERS was
35-fold stronger than it was with NBT-functionalized particles, but with
AuNST@Cy7.5 and AuNST@NBT, the SERS responses were similar. With all
nanoparticles tested, the SERS plasmonic profiles after 785 nm excitation were
slightly blue-shifted, as compared with the laser wavelength, possibly owing to
the inner filter effect. After 633-nm excitation, the SERS profiles were
redshifted, in agreement with EM theory. In all cases, the plasmonic EF
profiles were much broadened compared to the calculated ones and did not follow
the four-power law.