  A theory of flow stress (FS), reviewing and developing our research,e.g.
arxiv:1803.08247;1908.09338, is proposed,including yield strength (YS) of PC
materials for quasi-static plastic loading for grain of average size d in range
10^{-8}-10^{-2}m. It's based on statistical model of energy spectrum
distribution in each grain of 1-mode PC sample under plastic loading,with
highest level equal to maximal dislocation energy. Found distribution of scalar
dislocation density leads to FS due to Taylor strain hardening containing usual
and anomalous HP laws for coarse and NC grains, respectively, and reaches
maximum for extreme grain size d_0 of order 10^{-8}m. Maximum undergoes shift
to region of larger grains for decreasing T and increasing strains. Coincidence
is established among theoretical and experimental data on YS for
BCC(\alpha-Fe), FCC(Cu,Al,Ni),HCP(\alpha-Ti,Zr) PC materials at T=300K.The
T-dependence of strength quantities is studied. It is shown using Al that YS
grows with decrease in T for all grains with d>3d_0,and then YS decreases in NC
region,thus determining a temperature-dimension effect (TDE).1-phase model of
PC sample is extended by including softening GB phase into 2-phase model,and
then by dispersion (un)hardening. A quasi-particle interpretation of
crystallite energy quantization is suggested.Analytic and graphic forms of HP
laws are obtained in above samples with different values of small-,large-angle
GB and constant pores.The maximum of YS and respective extremal grain size of
the samples are shifted by change of 2-nd phase.The T-dependence of YS in range
of 150-350K for Al demonstrates the validity of TDE. An enlargement of 2-nd
phase neutralizes TDE.Deformation curves for 1- and 2-mode 2-phase \alpha-Fe PC
model are constructed with Backofen-Considere fracture criterion,as compared to
experimental,1-phase model data, and strongly depend on multimodality and GB