  Martensite damage in Dual-Phase (DP) steel has been studied extensively, yet,
the exact deformation mechanisms that trigger or inhibit damage initiation
remain mostly unexplored. Whereas generally assumed to be hard and brittle,
lath martensite in fact deforms in a highly anisotropic manner, showing large
strains under favorable habit plane orientations, which is attributed both to
the lath morphology and to so-called 'substructure boundary sliding'. Yet, the
correlation (or interplay) between plasticity and damage in lath martensite has
not received much attention. Therefore, we raise the question whether these
soft martensite plasticity mechanisms can delay or even inhibit damage
initiation. We analyze several 'damage-sensitive' martensite notches, {i.e.
thin contractions of two martensite islands,} by combining several
state-of-the-art experimental and analysis methods. Deformations are tracked
in-situ at the nanoscale, aligned to detailed microstructure maps, and
categorised, for each martensite variant, into habit plane or
out-of-habit-plane slip. In these experiments, strong plasticity (>70%) is
observed in martensite notches, enabled by slip along a favorably oriented
habit plane, whereas damaged notches have unfavorably oriented habit planes,
showing limited pre-damage strains (<10%), carried by out-of-habit-plane slip.
Additionally, one-to-one experimentally based Crystal Plasticity (CP)
simulations are performed in parallel, employing a recently introduced Enriched
CP approach which models a soft plasticity mechanism on the variants' habit
plane. The Enriched CP simulations show considerably lower hydrostatic stresses
in non-damaged and plastically deforming notches, thereby revealing that the
soft habit plane mechanism is key for introducing the high plastic anisotropy
that can lead to the inhibition of martensite damage in highly strained
martensite notches.