  The increasing relevance of energy storage technologies demands high-capacity
cathode materials for Li-ion batteries. Recently, Li-rich defect anti-fluorite
Li$_5$FeO$_4$ has emerged as a high-capacity cathode material exhibiting
simultaneous anionic and cationic redox without significant oxygen release. But
suffers from irreversible structural change and capacity fade during cycling.
Herein we investigate the suppressed capacity fade reported in Co substituted
Li$_5$FeO$_4$ and establish the optimal performance through tuning the
concentration and oxidation state of Co. We have substituted Co at the Fe site
and carried out a detailed analysis of structural, magnetic, electronic, and
electrochemical properties using first-principles density functional theory
calculations. The extended stability and suppressed capacity fading are found
only in specific compositions depending on the Co/Li concentration and the
oxidation state of Co. The reasons behind suppressed capacity fading in Co
substituted systems have been unveiled on the basis of bonding analyses and
proposed as a strategy to suppress the voltage fading reported in Li-rich
materials due to transition metal migration. From the evaluation of
thermodynamic stability and electronic structure,
Li$_{5.5}$Fe$_{0.5}$Co$_{0.5}$O$_4$, Li$_5$Fe$_{0.25}$Co$_{0.75}$O$_4$, and
Li$_{4.5}$Fe$_{0.5}$Co$_{0.5}$O$_4$ are found to exhibit better electrical
conductivity than Li$_5$FeO$_4$. All these systems have voltage in the range of
3 to 5 V and exhibit three dimensional Li diffusion pathway with a diffusion
barrier height of around 0.3 eV. From Li$_5$Fe$_{0.25}$Co$_{0.75}$O$_4$, one
can delithiate three Li-ions without structural change and oxygen release,
therefore expected to acquire a reversible capacity of around 513 mAh/g.
Moreover, as in pristine Li$_5$FeO$_4$, the selected Co substituted systems
also exhibit simultaneous anionic and cationic redox without significant O2
release.