  Evidence for High Tc cuprate superconductivity is found in a region of the
phase diagram where non-superconducting Fermi liquid metals are expected. Cu
valences estimated independently from both x-ray absorption near-edge structure
(XANES) and bond valence sum (BVS) measurements are > 2.3 for structures in the
homologous series (Cu0.75Mo0.25)Sr2(Y,Ce)sCu2O5+2s+{\delta} with s = 1, 2, 3,
and 4. The s = 1 member, (Cu0.75Mo0.25)Sr2YCu2O7+{\delta}, 0 \leq {\delta} \leq
0.5, is structurally related to YBa2Cu3O7 in which 25% of the basal Cu cations
[i.e. those in the chain layer] are replaced by Mo, and the Ba cations are
replaced by Sr. After oxidation under high pressure the s = 1 member becomes
superconducting with Tc = 88K. The Cu valence is estimated to be ~2.5, well
beyond the ~2.3 value for which other High-Tc cuprates are considered to be
overdoped Fermi liquids. The increase in valence is attributed to the
additional 0.5 oxygen ions added per chain upon oxidation. The record short
apical oxygen distance, at odds with current theory, suggests the possibility
of a new pairing mechanism but further experiments are urgently needed to
obtain more direct evidence. From the structural point of view the members with
s \geq 2 are considered to be equivalent to single-layer cuprates. All have Tc
~ 56 K which is significantly higher than expected because they also have
higher than expected Cu valences. The XANES-determined valences normalized to
give values in the CuO2 layers are 2.24, 2.25, and 2.26 for s = 2, 3, and 4,
while the BVS values determined for the valence in the CuO2 layer alone are
2.31-2.34 for the s = 2 and 3 members. No evidence for periodic ordering has
been detected by electron diffraction and high resolution imaging studies. The
possibility that the charge reservoir layers are able to screen long range
coulomb interactions and thus enhance Tc is discussed.