  We propose fabrication of the fiber-shaped lithium ion batteries assembled by
twisting a cathode filament together with an anode filament. The cathode
filament is fabricated by depositing a LiFePO4 (LFP)-composite layer onto a
steel-filled polyester conductive thread (SPCT). As anode filaments, we propose
several scenarios including a Li4Ti5O12 (LTO)-composite coated SPCT
(dip-and-dry deposition), a tin-coated SPCT (PVD deposition) as well as a bare
tin wire. An electrolyte composite layer consisting of LiPF6 and polyethylene
oxide (PEO) is then deposited onto both the anode and cathode filament before
the battery assembly. By twisting the cathode filament and anode filament
together using a customized jig, the batteries are then assembled. The
open-circuit voltage is found to be ~ 2.3 V for the battery using the LTO@SPCT
anode, and ~3.3 V for the battery using the tin@SPCT anode and the tin wire
anode. Charge-discharge tests are carried out at different C rates for each
battery sample. Experimental results suggest that the LIBs using the LTO@SPCT
anode, the tin@SPCT anode and the bare tin wire anode could achieve a specific
capacity of ~64, ~67, and ~96 mAh/g, respectively, when charge-discharged at
0.5-C rate. The battery could retain well its capacity after 80
charge-discharge cycles. During operation of all the batteries reported in this
paper, their coulombic efficiency remained above 80%. Among the advantages of
the proposed LIB are light weight, ease of fabrication, high specific
capacitance, high energy density, and good durability. Finally, employing cheap
and commercially-available steel-filled polyester threads as a base material in
our batteries, makes them potentially suitable for integration into wearables
using various standard textile manufacturing techniques.