  To improve the drying method in the manufacture of woodwind reeds, green
canes (Arundo donax L.) were dried under various humidity-temperature
conditions and the intensity of cell collapse was evaluated from the swelling
due to steaming involving the recovery of collapse. At 30 C, the intensity of
collapse was increased by slower drying. It was considered that: 1) slower
drying resulted in higher sample temperature in the early stage of drying to
increase the collapse; 2) rapid drying stiffened the surface of sample and such
"shell" prohibited the following collapse; 3) slower drying i.e. longer loading
of liquid tension caused more remarkable and/or frequent viscoelastic yields of
cells. Consequently the intensity of collapse increased when the cane was dried
from its waxy outer surface or in the presence of node: both of them retarded
the drying. On the other hand, higher drying temperature caused greater
intensity of collapse in spite of faster drying. It was suggested that the
thermal softening of cane cells leads to easier yield of the cell wall, at the
same time the rapid drying does not allow the recovery of collapse after the
disappearance of free water. These results indicated that faster drying at
lower temperature is preferable for drying cane with less collapse.