  Despite fascinating experimental results, the influence of defects and
elastic strains on the physical state of nanosized ferroelectrics is still
poorly explored theoretically. One of unresolved theoretical problems is the
analytical description of the strongly enhanced spontaneous polarization,
piezoelectric response, and dielectric properties of ferroelectric oxide thin
films and core-shell nanoparticles induced by elastic strains and stresses. In
particular, the 10-nm quasi-spherical BaTiO3 core-shell nanoparticles reveal a
giant spontaneous polarization up to 130 mu_C/cm2, where the physical origin is
a large Ti off-centering. The available theoretical description cannot explain
the giant spontaneous polarization observed in these spherical nanoparticles.
This work analyzes polar properties of BaTiO3 core-shell spherical
nanoparticles using the Landau-Ginzburg-Devonshire approach, which considers
the nonlinear electrostriction coupling and large Vegard strains in the shell.
We reveal that a spontaneous polarization greater than 50 mu_C/cm2 can be
stable in a (10-100) nm BaTiO3 core at room temperature, where a 5 nm
paraelectric shell is stretched by (3-6)% due to Vegard strains, which
contribute to the elastic mismatch at the core-shell interface. The
polarization value 50 mu_C/cm2 corresponds to high tetragonality ratios (1.02 -
1.04), which is further increased up to 100 mu_C/cm2 by higher Vegard strains
and/or intrinsic surface stresses leading to unphysically high tetragonality
ratios (1.08 - 1.16). The nonlinear electrostriction coupling and the elastic
mismatch at the core-shell interface are key physical factors of the
spontaneous polarization enhancement in the core. Doping with the
highly-polarized core-shell nanoparticles can be useful in optoelectronics and
nonlinear optics, electric field enhancement, reduced switching voltages,
catalysis, and electrocaloric nanocoolers.