  Density is one of the most commonly measured or estimated materials
properties, especially for glasses and melts that are of significant interest
to many fields, including metallurgy, geology, materials science and
sustainable cements. Here, two types of machine learning (ML) models (i.e.,
random forest (RF) and artificial neural network (ANN)) have been developed to
predict the room-temperature density of glasses in the compositional space of
CaO-MgO-Al2O3-SiO2-TiO2-FeO-Fe2O3-Na2O-K2O-MnO (CMASTFNKM), based on ~2100 data
points mined from ~140 literature studies. The results show that the RF and ANN
models give accurate predictions of glass density with R2 values, RMSE, and
MAPE of ~0.96-0.98, ~0.02-0.03 g/cm3 and ~0.59-0.79%, respectively, for the 15%
testing set, which are more accurate compared with empirical density models
based on ionic packing ratio (with R2 values, RMSE, and MAPE of ~0.28-0.91,
~0.05-0.15 g/cm3, and ~1.40-4.61%, respectively). Furthermore, glass density is
shown to be a reliable reactivity indicator for a range of CaO-Al2O3-SiO2 (CAS)
and volcanic glasses due to its strong correlation (R2 values above ~0.90) with
the average metal-oxygen dissociation energy (a structural descriptor) of these
glasses. Analysis of the predicted density-composition relationships from these
models (for selected compositional subspaces) suggests that the ANN model
exhibits a certain level of transferability (i.e., ability to extrapolate to
compositional space not (or less) covered in the database) and captures known
features including the mixed alkaline earth effects for
(CaO-MgO)0.5-(Al2O3-SiO2)0.5 glasses.