  Fractal dimension (D) is an effective parameter to represent the irregularity
and fragmental property of a self-affine surface, which is common in physical
vapor deposited thin films. D could be evaluated through the scaling
performance of surface roughness by using atomic force microscopy (AFM)
measurements, but lots of AFM images with different scales (L) are needed. In
this study, a surface roughness prediction (SRP) method was proposed to
evaluate D values of a single AFM image, in which the roughness at smaller L
was estimated by image segmentation with flatten modification. Firstly, a
series of artificial fractal surfaces with ideal dimension (Di) values ranging
from 2.1 to 2.9 were generated through Weierstrass-Mandelbrot (W-M) function,
in order to compare SRP method with traditional methods such as box counting
method and power spectral density method. The calculated dimension (Dc) by SRP
method was much closer to Di than the other methods, with a mean relative error
of only 0.64%. Secondly, SRP method was utilized to deal with real surfaces,
which were AFM images of amorphous alumina thin films with L of 1-70 {\mu}m. Dc
obtained by SRP method based on a single AFM image was also close to the result
in our previous study by multi-image analysis at L above 10 {\mu}m, while the
larger Dc at smaller L was consisted with the actual surface feature. The
validity of SRP method and the physics nature of real surfaces were discussed,
which might be helpful to obtain more understandings of fractal geometry.