  Organic photodetectors (OPDs) based on trap-assisted photomultiplication (PM)
effect with external quantum efficiency (EQE) far exceeding 100% are quite
appealing for achieving highly sensitive photodetection. A classic structure of
PM-type OPDs is based on the active layer of P3HT:PC70BM with the weight ratio
of 100:1, in which PC70BM forms islands and supply bulk electron traps for
inducing strong interfacial band bending and thus hole tunneling from the Al
electrode. In this paper, aiming for optimizing the PM effect, we study the
photogenerated carrier distribution by tuning thickness of the active layer
(P3HT:PC70BM). The combination effect of both the exciton generation and
exciton dissociation processes affects the photogenerated carrier distribution,
which ultimately determines the PM performances of OPDs. On the one hand,
simulation reveals that the thinner the active layer, the stronger exciton
generation near the Al electrode. On the other hand, the photoluminescence and
surface morphology studies reflect that the active layer with thickness of 230
nm has the smooth surface and produces the highest exciton dissociation rate.
The two effects result in the OPD with a 205 nm thick active layer has the
champion EQE (105569%) and photoresponsivity (344 A/W), corresponding to an
enhancement of 330% with respect to the OPD with a 325 nm thick active layer.
Ascribed to the trade off of EQE and dark current, the detectivity performs
differently at different wavelength ranges. At short wavelength range, the
detectivity reaches the highest when the active layer is 205 nm thick, while
the highest detectivity at long wavelength range is produced by the thickest
active layer. Our work contributes to developing low cost organic
photodetectors for detecting weak light signals.