  Refractory multi-element alloys (RMEA) with body-centered cubic (bcc)
structure have been the object of much research over the last decade due to
their high potential as candidate materials for high-temperature applications.
Most of these alloys display a remarkable strength at high temperatures, which
cannot be explained by the standard model of bcc plasticity dominated by
thermally-activated screw dislocation motion. Recent research on Nb-Mo-Ta-W
alloys points to a heightened role of edge dislocations on deformation, which
is generally attributed to atomic-level chemical fluctuations in the material
and their interactions with dislocation cores during slip. However, while this
model accounts for a strengthening effect due to the chemical complexity of the
alloy, it is not sufficient to explain its strength across the entire thermal
range. Here we propose a new mechanism that captures the existing theories
about enhanced lattice strengthening and a thermally-activated component that
emanates directly from the chemical complexity of the RMEA. This compositional
complexity results in unique vacancy formation energy distributions with tails
that extend into negative energies, leading to spontaneous, i.e., athermal,
vacancy formation at edge dislocation cores. These vacancies relax into
atomic-sized super-jogs on the dislocation line, acting as extra pinning points
that increase the activation stress of the dislocation. At the same time, these
super-jogs can displace diffusively along the glide direction, relieving with
their motion some of the extra stress, thus countering the hardening effect due
to jog-pinning. The interplay between these two processes as a function of
temperature confers an extra strength to edge dislocation at
intermediate-to-high temperatures, in remarkable agreement with experimental
measurements in Nb-Mo-Ta-W and across a number of different RMEA.