  The design of efficient electrocatalysts for electrochemical water splitting
with minimal amount of precious metal is crucial to attain renewable and
sustainable energy conversion. Here, we report the use of a network of CdSe
branched colloidal nanocrystals, made of a CdSe core and eight CdSe pods
(so-called octapods), able to host on their pods Pt particles, and thus
catalyzing water splitting reactions. Thanks to the octapod shape, the
resulting Pt-hosting network is mechanically trapped onto carbon nanotube
buckypaper, providing mechanically flexible and binder-free electrodes. We
found that such hierarchical configuration maximizes the mass activity and the
utilization efficiency of Pt for the hydrogen evolution reaction (HER). At a
potential of -0.15 V vs. reversible hydrogen electrode, the Pt/octapod
network-based electrodes display a Pt mass activity on the HER of 166 A mg-1
and 42 A mg-1 in acidic and alkaline media, respectively. These values
correspond to turnover frequencies of 168 s-1 and 42 s-1, respectively, which
are in that order 14 and 21 times higher compared to commercially available
Pt/C benchmarks. The strong chemical and mechanical interactions between the Pt
and the octapod surface, along with pod-aided adhesion of the Pt/octapod
network to the buckypaper, result in a long-term durability (>20 h) of the
HER-activity in both media. These results experimentally prove that the
exploitation of our network of branched nanocrystals hosting Pt particles can
circumvent the durability issues of the catalysts while adopting either
ultralow Pt loadings or benchmarking carbon-supported Pt nanocrystals. Our work
opens up prospects for using porous networks made by branched nanocrystals as
catalysts with ultralow amount of noble metals and controlled catalytic
properties.