  We have used Rietveld refinement technique to determine the extent of
intergrowth of Bi$_{2}$Sr$_{2}$CuO$_{6+x}$ phase and co-crystallization of
competing phases in a high temperature superconductor
Bi$_{2}$Sr$_{2}$CaCu$_{2}$O$_{8+x}$ (Bi-2212). The refinement was done on
powder diffractograms obtained on powders of Bi-2212 made by grinding single
crystals of Bi-2212 grown using two different self-flux techniques, namely
pressure technique (PT) and regrowth technique(RG). JANA and FullPROF programs
were used for refinement, both of which gave consistent results. Bi and Sr
atom's positions were refined in the average structure of centrosymmetric space
group $Bbmb$. To incorporate for Bi atoms modulation and modulation vector,
refinement was done in centrosymmetric space group
N$^{Bbmb}_{1\bar{1}1}$(Bbmb(0$\gamma$1)). It was found that the b* component of
the modulation vector decreased with a decrease in the superconducting
transition temperature in PT sample compared to the RG sample, suggesting a
better alignment of the CuO$_2$ planes with respect to Bi-O planes in PT
sample. All the samples were also found to exhibit strong preferred orientation
effect. Values of March-Dollase parameters corresponding to the preferred
orientation function were obtained. We also calculated Brindley absorption
contrast factors \textit{t}$_{\phi}$ and the effect of micro-absorption on the
quantity of phases present in each sample. A Rietveld refinement incorporating
all the factors resulted in exceptional values of goodness of fit parameters
for all the samples with the lowest value of 2.08 found for the PT sample
ground for 2 minutes. Additionally, the powders corresponding to the PT
crystals were found to have no co-crystallising phase and $\sim$ 94$\%$ Bi-2212
phase, suggesting that crystals grown by pressure technique are of extremely
good quality, much better than those grown by RG flux technique.