  In this investigation, we have synthesized thermally stable cubic
CsSnCl$_{3}$ perovskite nanocrystals (crystal size ~300 nm) with better surface
morphology by the hot-injection technique. Excellent crystalline quality of
these cubic nanocrystals was confirmed by high-resolution transmission electron
microscopy imaging. The binding of organic ligands on the surface of the sample
was characterized by nuclear magnetic resonance spectroscopy. The UV-visible
spectroscopy ensured that CsSnCl$_{3}$ nanocrystals have a direct bandgap of
~2.98 eV which was confirmed by steady-state photoluminescence spectroscopy.
The band edge positions calculated by the Mulliken electronegativity approach
predicted the potential photocatalytic capability of the nanocrystals which was
then experimentally confirmed by the photodegradation of RhB dye under visible
and UV-visible irradiation. Our theoretical calculation by employing the
generalized gradient approximation (GGA) and GGA + U methods demonstrated 90%
accurate estimation of experimentally observed optical bandgap when $U_{eff}$ =
6 eV was considered. The ratio of the effective masses of the hole and electron
expressed as D = $m_{h}^{*}/m_{e}^{*}$ was also calculated for $U_{eff}$ = 6
eV. Based on this theoretical calculation and experimental observation of the
photocatalytic performance of CsSnCl$_{3}$ nanocrystals, we have proposed a new
interpretation of the "D" value: a "D" value of either much smaller or much
larger than 1 is the indication of low recombination rate of the photogenerated
electron-hole pairs and the high photocatalytic efficiency of a photocatalyst.
We believe that this comprehensive investigation may be helpful for the
large-scale synthesis of thermally stable cubic CsSnCl$_{3}$ nanocrystals and
also for a greater understanding of their potential in photocatalytic,
photovoltaics and other prominent optoelectronic applications.