  Medium- and high-entropy alloys (M/HEAs) mix multiple principal elements with
near-equiatomic composition and represent a paradigm-shift strategy for
designing new materials for metallurgy, catalysis, and other fields. One of the
core hypotheses of M/HEAs is lattice distortion. However, experimentally
determining the 3D local lattice distortion in M/HEAs remains a challenge.
Additionally, the presumed random elemental mixing in M/HEAs has been
questioned by atomistic simulations, energy dispersive x-ray spectroscopy
(EDS), and electron diffraction, which suggest the existence of local chemical
order in M/HEAs. However, the 3D local chemical order has eluded direct
experimental observation since the EDS elemental maps integrate the composition
of atomic columns along the zone axes, and the diffuse reflections/streaks in
electron diffraction of M/HEAs may originate from planar defects. Here, we
determine the 3D atomic positions of M/HEA nanocrystals using atomic electron
tomography, and quantitatively characterize the local lattice distortion,
strain tensor, twin boundaries, dislocation cores, and chemical short-range
order (CSRO) with unprecedented 3D detail. We find that the local lattice
distortion and strain tensor in the HEAs are larger and more heterogeneous than
in the MEAs. We observe CSRO-mediated twinning in the MEAs. that is, twinning
occurs in energetically unfavoured CSRO regions but not in energetically
favoured CSRO ones. This observation confirms the atomistic simulation results
of the bulk CrCoNi MEA and represents the first experimental evidence of
correlating local chemical order with structural defects in any material
system. We expect that this work will not only expand our fundamental
understanding of this important class of materials, but also could provide the
foundation for tailoring M/HEA properties through lattice distortion and local
chemical order.