  Faradaic deionization (FDI) is a promising technology for energy-efficient
water desalination using porous electrodes containing redox-active materials.
Herein, we demonstrate for the first time the capability of a symmetric FDI
flow cell to produce freshwater (<17.1 mM NaCl) from concentrated brackish
water (118mM), to produce effluent near freshwater salinity (19.1 mM) from
influent with seawater-level salinity (496 mM), and to reduce the salinity of
hypersaline brine from 781 mM to 227 mM. These remarkable salt-removal levels
were enabled by using flow-through electrodes with high areal-loading of nickel
hexacyanoferrate (NiHCF) Prussian Blue analogue intercalation material. The
pumping energy consumption due to flow-through electrodes was mitigated by
embedding an interdigitated array of <100 $\mu$m wide channels in the
electrodes using laser micromachining. The micron-scale dimensions of the
resulting embedded, micro-interdigitated flow fields (e$\mu$-IDFFs) facilitate
flow-through electrodes with high apparent permeability while minimizing
active-material loss. Our modeling shows that these e$\mu$-IDFFs are more
suitable for our intercalation electrodes because they have >100X lower
permeability compared to common redox-flow battery electrodes, for which
millimetric flow-channel widths were used exclusively in the past. Total
desalination thermodynamic energy efficiency (TEE) was improved by more than
ten-fold relative to unpatterned electrodes: 40.0% TEE for brackish water,
11.7% TEE for hypersaline brine, and 7.4% TEE for seawater-salinity feeds.
Water transport between diluate and brine streams and charge efficiency losses
resulting from (electro)chemical effects are implicated as limiting energy
efficiency and water recovery, motivating their investigation for enhancing
future FDI performance.