  The plastic deformation processes that occur in a tensily deformed High
Density Polyethylene specimen were studied from full-field strain and strain
rate measurements obtained by 3D DIC (Digital Image Correlation).The tensile
tests were performed every 10{\textdegree}C from room temperature to
120{\textdegree}C . For temperatures below 60{\textdegree}C , it is shown that
the strain localization effect becomes less pronounced when the temperature
increases. For temperatures higher than 60{\textdegree}C , the material is
found to exhibit double yielding behavior. By analyzing the DIC data in
Lagrangian representation, it was possible to quantitatively highlight the
strain localization effect that is specifically associated with the second
yield. The second yield strain (E_{Y_2}) was measured and appeared to be
independent of temperature. For temperatures smaller than 60{\textdegree}C , it
was found that the threshold strain corresponding to (E_{Y_2}) also marks the
onset of the deformation process phase during which the volume strain strongly
increases. Based on previous studies of our research team and on literature we
concluded that the critical strain (E_{Y_2}) corresponds to the onset of the
lamellar morphology destruction. At high strain levels, the neck stabilization
phase was shown to proceed according to a strain driven scheme characterized by
threshold strains that are temperature independent. The experimental values of
the threshold strain marking the onset of the stabilization phase are found to
be in good agreement with those found using the Haward-Thackray model.