  Colloidal nanocrystals are a promising fluorescent class of materials, whose
spontaneous emission features can be tuned over a broad spectral range via
their composition, geometry and size. However, towards embedding nanocrystals
films in elaborated device geometries, one significant drawback is the
sensitivity of their emission properties on further fabrication processes like
lithography, metal or oxide deposition, etc. In this work, we demonstrate how
bright emitting and robust thin films can be obtained by combining nanocrystal
deposition from solutions via spin2 coating with subsequent atomic layer
deposition of alumina. For the resulting composite films, the layer thickness
can be controlled on the nanoscale, and their refractive index can be finely
tuned by the amount of deposited alumina. Ellipsometry is used to measure the
real and imaginary part of the dielectric permittivity, which gives direct
access to the wavelength dependent refractive index absorbance of the film.
Detailed analysis of the photophysics of thin films of core-shell nanocrystal
with different shape and different shell thickness allow to correlate the
behavior of the photoluminescence and of the decay life time to the changes in
the non-radiative rate that are induced by the alumina deposition. We show that
the photoemission properties of such composite films are stable in wavelength
and intensity over several months, and that the photoluminescence completely
recovers from heating processes up to 240$^\circ$C. The latter is particularly
interesting, since it demonstrates robustness to the typical heat treatment
that is needed in several process steps like resist-based lithography and
deposition by thermal or electron beam evaporation of metals or oxides.