  Finite element models of the thorax are under development to assist vehicle
safety researchers with the design of countermeasures such as advanced restrain
systems. Computational models have become more refined with increasing
geometrical complexity as element size decreases. These finite element models
can now capture small geometrical features with an attempt to predict fracture.
However, the bone material properties currently available, and in particular
the rate sensitivity, have been mainly determined from compression tests or
tests on long bones. There is a need for a new set of material properties for
the human rib cortical bone. With this objective, a new clamping technique was
developed to test small bone coupons under tensile loading. Ten coupons were
harvested from the cortical shell of the sixth and seventh left ribs from three
cadavers. The coupons were tested to fracture under quasi-static (target strain
rate of 0.07 %/s) and dynamic loading (target strain rate of 170 %/s). Prior to
testing, each coupon was imaged with a computed micro-tomograph to document the
bone microstructure. An optical method was used to determine the strain field
in the coupon for the quasi-static tests. The rib bone coupons were found to be
elastic, with brittle fracture. No plastic behavior was observed in this test
series. The bone coupons were assumed isotropic, homogeneous and elastic
linear, and the average Young's modulus for the quasi-static tests (13.5 GPa)
and the failure stresses (quasi-static: 112 MPa, dynamic: 124.6 MPa) were in
line with published data. Fracture however did not always occur in the gage
area where the cross-sectional area was the smallest, which contradicted the
assumption of isotropy and homogeneity. The comparison with material properties
obtained for long bones suggests that the effective cross-section has an effect
on the calculated material properties.