  Reduced titanium dioxide has recently attracted large attention, particularly
for its unique co-catalyst-free H$_2$ heterogeneous photocatalytic application.
The enhanced photocatalytic activity of the reduced TiO$_2$ was previously
ascribed to the introduction of point crystal defects (mainly Ti$_3^+$
centers), which result in the formation of intrinsic co-catalytic centers and
enhanced visible light absorption. In this work, we systematically investigate
the effect of different defects in the TiO$_{2-x}$ lattice on photocatalytic
H$_2$ evolution. To introduce different types of defects, thermal annealing in
air (oxidative), Ar (inert), Ar/H$_2$ (reducing), and H$_2$ (reducing)
atmospheres were performed on commercially available anatase nanopowder. Then,
the powders were characterized by scanning electron microscopy (SEM), X-ray
diffraction (XRD) and high-resolution transmission electron microscopy (HR-TEM)
to clarify the effect of treatment on material properties. Furthermore, the
defect types were characterized by electron paramagnetic resonance (EPR)
spectroscopy. We show that thermal annealing in different atmospheres can form
different amounts of different defect types in the TiO$_2$ structure. The
highest photocatalytic activation is achieved by annealing the anatase powder
in a reducing atmosphere for an appropriate temperature/annealing time. By
combining the results from H$_2$ generation and EPR analysis we show that the
simultaneous presence of two types of defects, i.e. surface exposed Ti$_3^+$
and lattice embedded Ti$_3^+$ centers, in an optimum low concentration, is the
determining factor for an optimized photocatalytic H$_2$ evolution rate. In
fact, annealing anatase powder under the so-reported optimized conditions in
reducing atmosphere leads to the generation of a considerable amount of H$_2$,
with rates as high as 338 $\mu$molh-1g-1.