  Simplified silica (Zeosil 1165 MP) and SBR (140k carrying silanol end-groups)
nanocomposites have been formulated by mixing of a reduced number of
ingredients with respect to industrial applications. The thermo-mechanical
history of the samples during the mixing process was monitored and adjusted to
identical final temperatures. The filler structure on large scales up to
micrometers was studied by transmission electron microscopy (TEM) and very
small-angle X-ray scattering (SAXS). A complete quantitative model extending
from the primary silica nanoparticle (of radius \approx 10 nm), to
nanoparticles aggregates, up to micrometer-sized branches with typical lateral
dimension of 150 nm is proposed. Image analysis of the TEM-pictures yields the
fraction of zones of pure polymer, which extend between the branches of a
large-scale filler network. This network is compatible with a fractal of
average dimension 2.4 as measured by scattering. On smaller length scales,
inside the branches, small silica aggregates are present. Their average radius
has been deduced from a Kratky analysis, and it ranges between 35 and 40 nm for
all silica fractions investigated here (\phi_si = 8-21% vol.). A central piece
of our analysis is the description of the interaggregate interaction by a
simulated structure factor for polydisperse spheres representing aggregates. A
polydispersity of 30% in aggregate size is assumed, and interactions between
these aggregates are described with a hard core repulsive potential. The same
distribution in size is used to evaluate the polydisperse form factor.
Comparison with the experimental intensity leads to the determination of the
average aggregate compacity (assumed identical for all aggregates in the
distribution, between 31% and 38% depending on \phi_si), and thus aggregation
number (ca. 45, with a large spread). Because of the effect of aggregate
compacity and of pure polymer zones, the volume fraction of aggregates is
higher in the branches than \phi_si. The repulsion between aggregates has a
strong effect on the apparent isothermal compressibility: it leads to a
characteristic low-q depression, which cannot be interpreted as aggregate mass
decrease in our data. In addition, the reinforcement effect of these silica
structures in the SBR-matrix is characterized with oscillatory shear and
described with a model based on the same aggregate compacity. Finally, our
results show that it is possible to analyze the complex structure of
interacting aggregates in nanocomposites of industrial origin in a
self-consistent and quantitative manner.