  Soft supramolecular materials are promising for the design of innovative and
highly tunable adhesives. These materials are composed of polymer chains
functionalized by strongly interacting moieties, sometimes called "stickers".
In order to systematically investigate the effect of the presence of
associative groups on the debonding properties of a supramolecular adhesive, a
series of supramolecular model systems has been characterized by probe-tack
tests. These model materials, composed of linear and low dispersity
poly(butylacrylate) chains functionalized in the middle by a single tri-urea
sticker, are able to self-associate by six hydrogen bonds and range in
molecular weight (M n) between 5 and 85 kg/mol. The linear rheology and the
nanostructure of the same materials (called "PnBA3U") was the object of a
previous study 1,2. At room temperature, the association of polymers via
hydrogen bonds induces the formation of rod-like aggregates structured into
bundles for M n \textless{} 40kg/mol and the behavior of a soft elastic
material was observed (G'\textgreater{}\textgreater{}G "and G'~$\omega$ 0). For
higher M n , the filaments were randomly oriented and polymers displayed a
crossover towards viscous behavior although terminal relaxation was not reached
in the experimental frequency window. All these materials show however similar
adhesive properties characterized by a cohesive mode of failure and low
debonding energies (W adh \textless{}40J/m 2 for a debonding speed of
100$\mu$m/s). The debonding mechanisms observed during the adhesion tests have
been investigated in detail with an Image tools analysis developed by our group
3. The measure of the projected area covered by cavities growing in the
adhesive layer during debonding can be used to estimate the true stress in the
walls of the cavities and thus, to characterize the in-situ large strain
deformation of the thin layer during the adhesion test itself. This analysis
revealed in particular that the PnBA3U materials with M n \textless{} 40 kg/mol
soften very markedly at large deformation like yield stress fluids, explaining
the low adhesion energies measured for these viscoelastic gels. 2