  Neutron diffraction and magnetic susceptibility studies show that
orthorhombic single-crystals of topological semimetals ${\rm
Sr(Mn_{0.9}Cu_{0.1})Sb_2}$ and ${\rm Sr(Mn_{0.9}Zn_{0.1})Sb_2}$ undergo three
dimensional C-type antiferromagnetic (AFM) ordering of the Mn$^{2+}$ moments at
$T_N = 200\pm10$ and $210\pm12$ K, respectively, significantly lower than that
of the parent SrMnSb$_2$ with $T_N=297 \pm 3$ K. Magnetization versus applied
magnetic field (perpendicular to MnSb planes) below $T_N$ exhibits slightly
modified de Haas van Alphen oscillations for the Zn-doped crystal as compared
to that of the parent compound. By contrast, the Cu-doped system does not show
de Haas van Alphen magnetic oscillations, suggesting that either Cu
substitution for Mn changes the electronic structure of the parent compound
substantially, or that the Cu sites are strong scatterers of carriers that
significantly shorten their mean free path thus diminishing the oscillations.
Density functional theory (DFT) calculations including spin-orbit coupling
predict the C-type AFM state for the parent, Cu-, and Zn-doped systems and
identify the $a$-axis (i.e., perpendicular to the Mn layer) as the easy
magnetization direction in the parent and 12.5% of Cu or Zn substitutions. In
contrast, 25% of Cu content changes the easy magnetization to the $b$-axis
(i.e., within the Mn layer). We find that the incorporation of Cu and Zn in
SrMnSb$_2$ tunes electronic bands near the Fermi level resulting in different
band topology and semi-metallicity. The parent and Zn-doped systems have
coexistence of electron and hole pockets with opened Dirac cone around the
Y-point whereas the Cu-doped system has dominant hole pockets around the Fermi
level with a distorted Dirac cone. The tunable electronic structure may point
out possibilities of rationalizing the experimentally observed de Haas van
Alphen magnetic oscillations.