  In this paper, we investigated the annealing experiments of
poly(mercaptopropylmethylsiloxane, PMMS) confined within two types of porous
templates (anodic aluminium oxide, AAO, and silica) characterized by different
pore diameter, d= 8-120nm, using different thermal protocols (varying
significantly in cooling/heating rate) by means of Broadband Dielectric
Spectroscopy (BDS) supported by the complementary Differential Scanning
Calorimetry (DSC) and temperature-dependent contact angle, {\theta},
measurements. It was found that relaxation times obtained from routine
temperature-dependent dielectric investigations deviate from the bulk behavior
when approaching the glass transition temperature. Importantly, this
confinement induced effect can be easily removed by the annealing experiments
performed at some specific range of temperatures. The analysis of the
dielectric data collected during isothermal experiments of confined samples
that was beforehand cooled with different rates revealed that (i) constant
rates of annealing gets longer with cooling and weakly depend on the rate of
cooling, and (ii) activation energy of the equilibration process, E_a, varies
with the reduction of the pore diameter and material the porous template is
made of. In fact, there is significant reduction in E_a from ~62 to ~23 kJ/mol
obtained for the annealing process carried out in AAO (d= 10 nm) and silica (d=
8 nm) membranes, respectively. Such significant change in E_a can be explained
taking into account temperature-dependence of {\theta} of PMMS indicating a
notable change in wettability between both surfaces upon cooling. As a
consequence, one can expect that the mass exchange between interfacial and core
molecules as well as adsorption-desorption processes occurring at the interface
at lower temperatures must be affected.