  Celitement is a new type of cement that is based on hydraulic
calcium-hydrosilicate (hCHS) that possesses a potential for minimizing the
ratio C/S from above 3 in OPC down to 1, which significantly reduces the amount
of CO$_2$ released during processing. The reaction kinetics of hCHS differs
from that of classical clinker phases due to the presence of highly reactive
silicate species, which involve silanol groups instead of pure calcium
silicates and aluminates and aluminoferrites. In contrast to Portland cement,
no calcium hydroxide is formed during hydration, which otherwise regulates the
Ca concentration. Without the buffering role of Ca(OH)$_2$ the concentration of
the dissolved species c(Ca$^{2+}$) and c(SiO$_4^{4-}$) and the corresponding pH
must be controlled to ensure a reproducible reaction. Pure hCHS reacts
isochemically with water, resulting in a C-S-H phase with the same chemical
composition as a single hydration product, with a homogeneous distribution of
the main elements Ca and Si throughout the sample. Here we study via
nanoindentation the mechanical properties of two different types of hardened
pastes made out of Celitement (C/S=1.28), with varying amounts of hCHS and
variable water to cement ratio. We couple nanoindentation grids with Raman
mappings to link the nanoscale mechanical properties to individual
microstructural components, yielding in-depth insight into the mechanics of the
mineralogical phases constituting the hardened cement paste. We show that we
can identify in hardened Celitement paste both fresh C-S-H with varying
density, and C-S-H from the raw material using their specific Raman spectra,
while simultaneously measuring their mechanical properties. Albeit not suitable
for phase identification, EDX measurements provide valuable information about
the distribution of alkalis, thus further helping to understand the reaction
pattern of hCHS.