  Plateaus in water adsorption isotherms on hydroxylated BeO surfaces suggest
significant differences between the hydroxylated (100) and (001) surface
structures and reactivities. Density functional theory structures and energies
clarify these differences. Using relaxed surface energies, a Wulff construction
yields a prism crystal shape exposing long (100) sides and much smaller (001)
faces. This is consistent with the BeO prisms observed when beryllium metal is
oxidized. A water oxygen atom binds to a single surface beryllium ion in the
preferred adsorption geometry on either surface. The water oxygen/beryllium
bonding is stronger on the surface with greater beryllium atom exposure, namely
the less-stable (001) surface. Water/beryllium coordination facilitates water
dissociation. On the (001) surface, the dissociation products are a hydroxide
bridging two beryllium ions and a metal coordinated hydride with some surface
charge depletion. On the (100) surface, water dissociates into a hydroxide
ligating a Be atom and a proton coordinated to a surface oxygen but the lowest
energy water state on the (100) surface is the undissociated metal-coordinated
water. The (100) fully hydroxylated surface structure has a hydrogen bonding
network which facilitates rapid proton shuffling within the network. The
corresponding (001) hydroxylated surface is fairly open and lacks internal
hydrogen bonding. This supports previous experimental interpretations of the
step in water adsorption isotherms. Further, when the (100) surface is heated
to 1000 K, hydroxides and protons associate and water desorbs. The more open
(001) hydroxylated surface is stable at 1000 K. This is consistent with the
experimental disappearance of the isotherm step when heating to 973 K.