  In this paper, we report the synthesis of reduced Graphene Oxide-Tin Oxide
nanocomposite and the effectiveness of this composite in decolorizing and
degrading Methylene Blue (MB). Tin Oxide was prepared by liquid phase
co-precipitation method and reduced Graphene Oxide-Tin Oxide (rGO-SnO2)
nanocomposite was prepared by solution mixing method. Tin Oxide nanoparticles
(NPs) have been ardently investigated as photocatalyst for water purification
and environment decontamination but the photon generated electron and hole pair
(EHP) recombination is one of the limiting factors. Reduced Graphene Oxide-Tin
Oxide (rGO-SnO2) nanocomposite is very efficient to overcome this limitation
for photocatalytic application. The as-synthesized GO, SnO2, GO-SnO2, rGO and
rGO-SnO2 nanocomposite were characterized by X-ray Diffraction, Scanning
Electron Microscopy, Energy Dispersive X-ray spectroscopy and Fourier Transform
Infrared spectroscopy. The XRD data confirms the sharp peak at 2Theta=10.44
degree corresponding to (002) reflection of GO with interlayer d spacing of
8.46 Angstrom indication of successful preparation of GO by oxidation of
graphite. Moreover, the diffraction peak shifts from 2Theta=10.44 degree to
2Theta=23.31 degree confirm successful synthesis of rGO as well. SEM image
shows the morphology of all the photocatalysts. EDX studies are carried out to
investigate the elemental composition and purity of the sample by giving all
the elements present in the nanomaterials. The presence of functional groups
was identified by FTIR. The rGO-SnO2 (1:10) nanocomposite shows an efficient
photodegradation efficiency of ~94% and ~95% under natural sunlight and UV
light irradiation respectively for Methylene Blue (MB) within 15 minutes.
Furthermore, the degradation kinetics of MB is also studied in this paper as
well.