  Ion-beam sputtering has been used to prepare Fe/Si multilayers on a variety
of substrates and over a wide range of temperatures. Small-angle x-ray
diffraction and transmission electron microscopy experiments show that the
layers are heavily intermixed although a composition gradient is maintained.
When the spacer layer is an amorphous iron silicide, the magnetic properties of
the multilayers are similar to those of bulk Fe. When the spacer layer is a
crystalline silicide with the B2 or DO$_3$ structure, the multilayers show
antiferromagnetic interlayer coupling like that observed in
ferromagnet/paramagnet multilayers such as Fe/Cr and Co/Cu. Depending on the
substrate type and the growth temperature, the multilayers grow in either the
(011) or (001) texture. The occurrence of the antiferromagnetic interlayer
coupling is dependent on the crystallinity of the iron and iron silicide
layers, but does not seem to be strongly affected by the perfection of the
layering or the orientation of the film. Since the B2- and DO$_3$-structure
Fe$\rm _x$Si$\rm _{1-x}$ compounds are known to be metallic, antiferromagnetic
interlayer coupling in Fe/Si multilayers probably originates from the same
quantum-well and Fermi surface effects as in Fe/Cr and Co/Cu multilayers.