  The strength of the lithosphere is typically modelled based on constitutive
equations for steady-state flow. However, models of lithospheric flexure reveal
differences in lithospheric strength that are difficult to reconcile based on
such flow laws. Recent rheological data from low-temperature deformation
experiments on olivine suggest that this discrepancy may be largely explained
by strain hardening. Details of the mechanical data, specifically the effects
of temperature-independent back stresses stored in the samples, indicate that
strain hardening in olivine occurs primarily due to long-range elastic
interactions between dislocations. These interpretations provided the basis for
a new flow law that incorporates hardening by development of back stress. Here,
we test this hypothesis by examining the microstructures of olivine samples
deformed plastically at room temperature either in a deformation-DIA apparatus
at differential stresses of < 4.3 GPa or in a nanoindenter at applied contact
stresses of > 10.2 GPa. High-angular resolution electron backscatter
diffraction maps reveal the presence of geometrically necessary dislocations
with densities commonly above 10$^{14}$ m$^{-2}$ and intragranular
heterogeneities in residual stress on the order of 1 GPa in both sets of
samples. Scanning transmission electron micrographs reveal straight
dislocations aligned along slip bands and interacting with dislocations of
other types that act as obstacles. The stress heterogeneities and accumulations
of dislocations along their slip planes are consistent with strain hardening
resulting from long-range back-stresses acting between dislocations. These
results corroborate the mechanical data in supporting the form of the new flow
law for low-temperature plasticity and provide new microstructural criteria for
identifying the operation of this deformation mechanism in natural samples.