  We investigate the dependence of magnetic properties on the out-of-plane
disorder strength $\Delta$, dipolar interaction strength $h^{}_d$ in
two-dimensional ($l^{}_x\times l^{}_y$) ensembles of nanoparticles using
numerical simulations. Such positional defects are redundantly observed in
experiments. The superparamagnetic character is dominant with negligible and
weak interaction strength $h^{}_d$, irrespective of $\Delta$ and aspect ratio
of the system $A^{}_r=l^{}_y/l^{}_x$. The double-loop hysteresis curve,
characteristics of antiferromagnetic coupling dominance, emerges with large
$h^{}_d$ and $\Delta(\%)\leq5$ in the square-like nanoparticles' assays.
Remarkably, the dipolar interaction of sufficient strength drives the magnetic
order from antiferromagnetic to ferromagnetic with large $\Delta$ and
$A^{}_r\leq4.0$, resulting in an enhancement in the hysteresis loop area. On
the other hand, the ferromagnetic coupling gets increased with $h^{}_d$ in
systems with huge $A^{}_r$. Consequently, the hysteresis loop is enormous, even
with moderate $h^{}_d$. The variation of the coercive field $\mu^{}_oH^{}_c$,
remanence $M^{}_r$, and amount of heat released $E^{}_H$ (due to the
hysteresis) with these parameters also suggests the transformation of nature
dipolar interaction. They are significant even with large $h^{}_d$ and smaller
$A^{}_r$, indicating the antiferromagnetic coupling dominance. Interestingly,
there is an enhancement in these with $\Delta$ and large $h^{}_d$ due to
ferromagnetic interaction. Notably, they are very significant even with
moderate $h^{}_d$ in the highly anisotropic system and external field along the
long axis of the sample. These results could help the experimentalist in
explaining the unusual hysteresis characteristics observed in such systems and
should also be beneficial in diverse applications such as data storage,
magnetic hyperthermia, etc.