  The Ni-base superalloy 718 is the most widely used material for
turbomachinery in the aerospace industry and land-based turbines. Although the
relationship between processing and the resulting properties is well known, an
understanding of the specific deformation mechanisms activated across its
application temperature range is required to create more mechanistically
accurate property models. Direct atomic-scale imaging observations with high
angle annular dark-field scanning transmission electron microscopy,
complemented by phase-field modeling informed by generalized stacking fault
surface calculations using density functional theory, were employed to
understand the shear process of ${\gamma}''$ and ${\gamma}'/{\gamma}''$
co-precipitates after 1 \% macroscopic strain at lower temperature (ambient and
$427 {\deg}C$). Experimentally, intrinsic stacking faults were observed in the
${\gamma}''$, whereas the ${\gamma}'$ was found to exhibit anti-phase
boundaries or superlattice intrinsic stacking faults. Additionally, the
atomically flat ${\gamma}'/{\gamma}''$ interfaces in the co-precipitates were
found to exhibit offsets after shearing, which can be used as tracers for the
deformation events. Phase-field modeling shows that the developing
fault-structure is dependent on the direction of the Burgers vector of the $a/2
\langle110\rangle$ matrix dislocation (or dislocation group) due to the lower
crystal symmetry of the ${\gamma''}$ phase. The interplay between ${\gamma}'$
and ${\gamma}''$ phases results in unique deformation pathways of the
co-precipitate and increases the shear resistance. Consistent with the
experimental observations, the simulation results indicate that complex
shearing mechanisms are active in the low-temperature deformation regime and
that multiple $a/2 \langle110\rangle$ dislocations of non-parallel Burgers
vectors may be active on the same slip plane.