  While of paramount importance in material science, the dynamics of cracks
still lacks a complete physical explanation. The transition from their slow
creep behavior to a fast propagation regime is a notable key, as it leads to
full material failure if the size of a fast avalanche reaches that of the
system. We here show that a simple thermodynamics approach can actually account
for such complex crack dynamics, and in particular for the non-monotonic
force-velocity curves commonly observed in mechanical tests on various
materials. We consider a thermally activated failure process that is coupled
with the production and the diffusion of heat at the fracture tip. In this
framework, the rise in temperature only affects the sub-critical crack dynamics
and not the mechanical properties of the material. We show that this
description can quantitatively reproduce the rupture of two different polymeric
materials (namely, the mode I opening of polymethylmethacrylate (PMMA) plates,
and the peeling of pressure sensitive adhesive (PSA) tapes), from the very slow
to the very fast fracturing regimes, over seven to nine decades of crack
propagation velocities. In particular, the fastest regime is obtained with an
increase of temperature of thousands of kelvins, on the molecular scale around
the crack tip. Although surprising, such an extreme temperature is actually
consistent with different experimental observations that accompany the fast
propagation of cracks, namely, fractoluminescence (i.e., the emission of
visible light during rupture) and a complex morphology of post-mortem fracture
surfaces, which could be due to the sublimation of bubbles.