  The crystal growth velocity is one thermodynamic parameter of solidification
experiments of undercooled melts under non-equilibrium conditions, which is
directly accessible to observation. We applied the electrostatic levitation
technique in order to study the crystal growth velocity $v$ as a function of
the undercooling $\Delta T$ for the intermetallic, congruently melting binary
alloy NiTi and the glass forming alloy Cu--Zr, as well as for the Zr-based
ternary alloys (Cu$_{\mathrm{x}}$Ni$_{\mathrm{1-x}}$)Zr ($x= 0.7, 0.6$) and the
Ni-based ternary alloy Ni(Zr$_{\mathrm{x}}$Ti$_{\mathrm{1-x}}) (x= 0.5)$. All
investigated systems within this work, except the eutectics $Cu_{56}Zr_{44}$
and $Cu_{46}Zr_{54}$, exceeded the hypercooling limit $\Delta T_{\mathrm{hyp}}$
and, remarkably, every $v(\Delta T)$ relation changed significantly at $\Delta
T_{\mathrm{hyp}}$. Our results for glass forming CuZr indicate that the
influence of the diffusion coefficient $D(T)$ on $v(\Delta T)$ at high
undercoolings, as claimed in literature, cannot be the sole reason for the
existence of a maximum in the $v(\Delta T)$ behaviour. These observations could
make a valuable contribution concerning an extension of growth theories to
undercooling temperatures $\Delta T > \Delta T_{\mathrm{hyp}}$. Nevertheless,
our finding has direct consequences to various disciplines, as our earth and
all living beings are examples for non-equilibrium systems. The scatter of our
velocity data is at least two orders of magnitude smaller than measurements
performed by former works due to our experimental setup, which allowed precise
contactless triggering at a specific undercooling, and our analysis method,
which considered the respective solidification morphologies.