  Conventional drying of colloidal materials and gels (including cement) can
lead to detrimental effects due to the buildup of internal stresses as water
evaporates from the nano/microscopic pores. However, the underlying nanoscopic
alterations in these gel materials that are, in part, responsible for
macroscopically-measured strain values, especially at low relative humidity,
remain a topic of open debate in the literature. In this study, sodium-based
calcium-alumino-silicate-hydrate (C-(N)-A-S-H) gel, the major binding phase of
silicate-activated blast furnace slag (one type of low-CO$_2$ cement), is
investigated from a drying perspective, since it is known to suffer extensively
from drying-induced microcracking. By employing in situ synchrotron X-ray total
scattering measurements and pair distribution function (PDF) analysis we show
that the significant contributing factor to the strain development in this
material at extremely low relative humidity (0%) is the local atomic structural
rearrangement of the C-(N)-A-S-H gel, including collapse of interlayer spacing
and slight disintegration of the gel. Moreover, analysis of the medium range
(1.0 - 2.2 nm) ordering in the PDF data reveals that the PDF-derived strain
values are in much closer agreement (same order of magnitude) with the
macroscopically measured strain data, compared to previous results based on
reciprocal space X-ray diffraction data. From a mitigation standpoint, we show
that small amounts of ZrO$_2$ nanoparticles are able to actively reinforce the
structure of silicate-activated slag during drying, preventing atomic level
strains from developing. Mechanistically, these nanoparticles induce growth of
a silica-rich gel during drying, which, via density functional theory
calculations, we show is attributed to the high surface reactivity of
tetragonal ZrO$_2$.