  Hybrid systems composed of the reduced graphene oxide-supported platinum and
multiwall carbon nanotubes-supported iridium (both noble metals utilized at low
loadings on the level of 15 and < 5 microg cm-2, respectively) have been
considered as catalytic materials for the reduction of oxygen in acid media
(0.5 mol dm-3 H2SO4). The electrocatalytic activity toward reduction of oxygen
and formation of hydrogen peroxide intermediate have been tested using rotating
ring-disk electrode voltammetric experiments. The efficiency of the proposed
catalytic systems has also been addressed by performing galvanodynamic
measurements with gas diffusion electrode half-cell at 80 {\deg}C. The role of
carbon nanotubes is to improve charge distribution at the electrocatalytic
interface and facilitate the transport of oxygen and electrolyte in the
catalytic systems by lowering the extent of reduced graphene oxide restacking
during solvent evaporation. The diagnostic electrochemical experiments reveal
that at iridium-containing systems not only higher disk currents, but also much
smaller ring currents have been produced (compared to reduced graphene
oxide-supported platinum and its composite with bare carbon nanotubes), clearly
implying formation of lower amounts of the undesirable hydrogen peroxide
intermediate. The enhancement effect coming from the addition of traces of
iridium (supported onto carbon nanotubes) to Pt, utilized at low loading, may
originate from the high ability of Ir to induce decomposition of the
undesirable hydrogen peroxide intermediate. There is a competition between
activation (due to the presence of small amounts of Ir) and dilution (by carbon
nanotubes) of Pt active centers in hybrid systems, therefore special attention
is paid to the adjustment of their composition.