  Germanium telluride (GeTe), a phase-change material, is known to exhibit four
different structural phases: three at room temperature (one amorphous and two
crystalline, $\alpha$ and $\gamma$) and one at high temperature (crystalline
$\beta$). Because transitions between the amorphous and crystalline phases lead
to significant changes in material properties (e.g., refractive index and
resistivity), GeTe has been investigated as a phase-change material for
photonics, thermoelectrics, ferroelectrics, and spintronics. Consequently, the
temperature-dependent phase transitions in GeTe have been studied for bulk and
thin-film GeTe, both fabricated by sputtering. Colloidal synthesis of
nanoparticles offers a more flexible fabrication approach for amorphous and
crystalline GeTe. These nanoparticles are known to exhibit size-dependent
properties, such as an increased crystallization temperature for the
amorphous-to-$\alpha$ transition in sub-10\,nm GeTe particles. The
$\alpha$-to-$\beta$ phase transition is also expected to vary with size, but
this effect has not yet been investigated for GeTe. Here, we report
time-resolved X-ray diffraction of GeTe nanoparticles with different diameters
and from different synthetic protocols. We observe a non-volatile
amorphous-to-$\alpha$ transition between 210$^{\circ}$C and 240$^{\circ}$C and
a volatile $\alpha$-to-$\beta$ transition between 370$^{\circ}$C and
420$^{\circ}$C. The latter transition was reversible and repeatable. While the
transition temperatures are shifted relative to the values known for bulk GeTe,
the nanoparticle-based samples still exhibit the same structural phases
reported for sputtered GeTe. Thus, colloidal GeTe maintains the same general
phase behavior as bulk GeTe while allowing for more flexible and accessible
fabrication. Therefore, nanoparticle-based GeTe films show great potential for
applications, such as in active photonics.