  Heusler compounds form a numerous class of intermetallics, which include two
families of compositions ABC and AB2C, usually referred to as half- and
full-Heusler compounds, respectively. Given their tunable electronic
properties, made possible by adjusting the chemical composition, these
materials are currently considered for the possible use in sustainable
technologies such as solar energy and thermoelectric conversion. According to
theoretical predictions, Sb substitution in the TiFe2Sn full-Heusler compound
is thought to yield band structure modifications that should enhance the
thermoelectric power factor. In this work we tested the phase stability and the
structural and microstructural properties of such heavily-doped compounds. We
synthesized polycrystalline TiFe2Sn1-xSbx samples (x=0,0.1,0.2 and 1.0) by arc
melting, followed annealing. The structural characterization, performed by
x-ray powder diffraction and microscopy analyses, confirmed the formation of
the Heusler AB2C structure (cF16, Fm-3m, prototype: MnCu2Al) in all samples,
with only few percent amounts of secondary phases and only slight deviations
from nominal stoichiometry. With increasing Sb substitution we found a steady
decrease of the lattice parameter, confirming that the replacement takes place
at the Sn site. Quite unusually, the as cast samples exhibited a higher lattice
contraction than the annealed ones. The fully substituted x=1.0 compound, again
adopting the MnCu2Al structure, does not form as stoichiometric phase and
turned out to be strongly Fe deficient.The physical behavior at room
temperature indicated that annealing with increasing temperature is beneficial
for electrical and thermoelectrical transport. Moreover, we measured a slight
improvement of electrical and thermoelectrical properties in the x=0.1 sample
and a suppression in the x=0.2 sample, as compared to the undoped x=0 sample.