  Some implants have approximately a lifetime of 15 years. The femoral stem,
for example, should be made of 316L/316LN stainless steel. Fretting corrosion,
friction under small displacements, should occur during human gait, due to
repeated loadings and un-loadings, between stainless steel and bone for
instance. Some experimental investigations of fretting corrosion have been
practiced. As well known, metallic alloys and especially stainless steels are
covered with a passive film that prevents from the corrosion and degradation.
This passive layer of few nanometers, at ambient temperature, is the key of our
civilization according to some authors. This work is dedicated to predict the
passive layer thicknesses of stainless steel under fretting corrosion with a
specific emphasis on the role of proteins. The model is based on the Point
Defect Model (micro scale) and an update of the model on the friction process
(micro-macro scale). Genetic algorithm was used for finding solution of the
problem. The major results are, as expected from experimental results, albumin
prevents from degradation at the lowest concentration of chlorides; an
incubation time is necessary for degrading the passive film; under fretting
corrosion and high concentration of chlorides the passive behavior is
annihilated.
  Les implants orthop\'ediques de hanche ont une dur\'ee de vie d'environ 15
ans. Par exemple, la tige f\'emorale d'un tel implant peut \^etre r\'ealis\'ee
en acier inoxydable 316L ou 316LN. Le fretting corrosion, frottement sous
petits d\'eplacements, peut se produire pendant la marche humaine en raison des
chargements r\'ep\'et\'es entre le m\'etal de la proth\`ese et l'os. Plusieurs
investigations exp\'erimentales du fretting corrosion ont \'et\'e entreprises.
Cette couche passive de quelques nanom\`etres, \`a temp\'erature ambiante, est
le point clef sur lequel repose le d\'eveloppement de notre civilisation, selon
certains auteurs. Ce travail vise \`a pr\'edire les \'epaisseurs de cette
couche passive de l'acier inoxydable soumis au fretting corrosion, avec une
attention sp\'ecifique sur le r\^ole des prot\'eines. Le mod\`ele utilis\'e est
bas\'e sur le Point Defect Model, PDM (\`a une \'echelle microscopique) et une
am\'elioration de ce mod\`ele en prenant en compte le processus de frottement
sous petits d\'ebattements. L'algorithme g\'en\'etique a \'et\'e utilis\'e pour
optimiser la convergence du probl\`eme. Les r\'esultats les plus importants
sont, comme d\'emontr\'e avec les essais exp\'erimentaux, que l'albumine, la
prot\'eine \'etudi\'ee, emp\^eche les d\'egradations de l'acier inoxydable aux
plus faibles concentrations d'ions chlorure ; ensuite, aux plus fortes
concentrations de chlorures, un temps d'incubation est n\'ecessaire pour
d\'etruire le film passif.