  This research describes the use of surface-enhanced Raman spectroscopy (SERS)
substrates based on colloidal silver nanoparticles (AgNPs) produced by laser
ablation of silver granules in pure water that are inexpensive, easy to make,
and chemically stable. Here, the effects of the laser power, pulse repetition
frequency, and ablation duration on the Surface Plasmon Resonance peak of AgNPs
solutions, were used to determine the optimal parameters. Also, the effects of
the laser ablation time on both ablation efficiency and SERS enhancement were
studied. The synthesized AgNPs were characterized by UV-Vis spectrophotometer
and Raman spectrometer. The Surface Plasmon Resonance peak of AgNP solutions
was centered at 404 nm confirming their synthesis. Using Raman spectroscopy,
they had main bands centered at 196, 568, 824, 1060, 1312 cm-1, 1538 and 2350
cm-1. Their Raman spectral profiles remained constant within the first few days
of storage at room temperature implying chemical stability. The Raman signals
from blood were enhanced when mixed with AgNPs and this depended on colloidal
AgNPs concentration. Using those generated by 12 hrs ablation time, an
enhancement of 14.95 was achieved. Additionally, these substrates had an
insignificant impact on the Raman profiles of samples of rat blood when mixed
with them. The Raman peaks noted were 932, 1064, 1190, 1338, 1410, 1650 and
2122 cm-1. These SERS substrates can be applied to areas such as forensics,
monitoring of the efficacy of drugs, disease diagnostics and pathogen
detection. All this can be achieved by comparing the Raman spectra of the
biological samples mixed with the synthesized SERS substrates for different
samples. Thus, the results on the use of inexpensive, simple-to-prepare Raman
substrates have the possibility of making surface-enhanced Raman spectroscopy
available to laboratories with scarce resources in developing nations.