  Predicting the dramatic changes in material properties caused by irradiation
damage is key for the design of future nuclear fission and fusion reactors.
Self-ion implantation is an attractive tool for mimicking the effects of
neutron irradiation. However, the damaged layer of implanted samples is only
few microns thick, making it difficult to estimate macroscopic properties. Here
we address this challenge using a combination of experimental and modelling
techniques. We concentrate on self-ion-implanted tungsten, the front-runner for
fusion armour components and a prototypical bcc material. To capture
dose-dependent evolution of properties, we experimentally characterise samples
with damage levels from 0.01 to 1 dpa. Spherical nano-indentation of <001>
grains shows hardness increasing up to a dose of 0.032 dpa, beyond which it
saturates. AFM measurements show pile-up increasing up to the same dose, beyond
which large pile-up and slip-steps are seen. Based on the observations we
develop a crystal plasticity (CPFE) model for the irradiated material. It
captures irradiation-induced hardening followed by strain-softening through
interaction of irradiation-defects and gliding dislocations. Shear resistance
of irradiation-defects is derived from TEM observations of similarly irradiated
samples. Nano-indentation of pristine and implanted tungsten of doses 0.01,
0.1, 0.32 and 1 dpa is simulated. Two model parameters are fitted to the
experimental results of the 0.01 dpa sample and are kept unchanged for all
other doses. Peak load, indent surface profiles and damage saturation predicted
by the CPFE model closely match experimental observations. Predicted lattice
distortions and dislocation distributions around indents agree with
corresponding measurements from HR-EBSD. Finally, the CPFE model is used to
predict the macroscopic stress-strain response of similarly irradiated bulk
tungsten material.