  The crystalline structure, magnetism, and magnetocaloric effect of a
GdCrO$_3$ single crystal grown with the laser-diode-heated floating-zone
technique have been studied. The GdCrO$_3$ single crystal crystallizes into an
orthorhombic structure with the space group $Pmnb$ at room temperature. Upon
cooling, under a magnetic field of 0.1 T, it undergoes a magnetic phase
transition at $T_{\textrm{N-Cr}} =$ 169.28(2) K with Cr$^{3+}$ ions forming a
canted antiferromagnetic (AFM) structure, accompanied by a weak ferromagnetism.
Subsequently, a spin reorientation takes place at $T_{\textrm{SR}} =$ 5.18(2) K
due to Gd$^{3+}$-Cr$^{3+}$ magnetic couplings. Finally, the long-range AFM
order of Gd$^{3+}$ ions establishes at $T_{\textrm{N-Gd}} =$ 2.10(2) K. Taking
into account the temperature-(in)dependent components of Cr$^{3+}$ moments, we
obtained an ideal model for describing the paramagnetic behavior of Gd$^{3+}$
ions within 30--140 K. We observed a magnetic reversal (positive $\rightarrow$
negative $\rightarrow$ positive) at 50 Oe with a minimum centering around 162
K. In the studied temperature range of 1.8-300 K, there exists a strong
competition between magnetic susceptibilities of Gd$^{3+}$ and Cr$^{3+}$ ions,
leading to puzzling magnetic phenomena. We have built the
magnetic-field-dependent phase diagrams of $T_{\textrm{N-Gd}}$,
$T_{\textrm{SR}}$, and $T_{\textrm{N-Cr}}$, shedding light on the nature of the
intriguing magnetism. Moreover, we calculated the magnetic entropy change and
obtained a maximum value at 6 K and ${\Delta}{\mu}_0H$ = 14 T, i.e.,
-${\Delta}S_{\textrm{M}} \approx$ 57.5 J/kg K. Among all RCrO$_3$ (R = $4f^n$
rare earths, $n =$ 7-14) compounds, the single-crystal GdCrO$_3$ compound
exhibits the highest magnetic entropy change, as well as an enhanced adiabatic
temperature, creating a prominent magnetocaloric effect for potential
application in magnetic refrigeration.