  Chemical crosslinking of collagen is a general strategy to reproduce
macroscale tissue properties in physiological environment. However,
simultaneous control of protein conformation, material properties and
biofunctionality is highly challenging with current synthetic strategies.
Consequently, the potentially-diverse clinical applications of collagen-based
biomaterials cannot be fully realised. In order to establish defined
biomacromolecular systems for mineralised tissue applications, type I collagen
was functionalised with 1,3-Phenylenediacetic acid (Ph) and investigated at the
molecular, macroscopic and functional levels. Preserved triple helix
conformation was observed in obtained covalent networks via ATR-FTIR and WAXS,
while network crosslinking degree could be adjusted based on specific reaction
conditions. Decreased swelling ratio and increased thermo-mechanical properties
were observed compared to state of-the-art carbodiimide (EDC)-crosslinked
collagen controls, likely related to the intermolecular covalent incorporation
of the aromatic segment. Ph crosslinked hydrogels displayed nearly intact
material integrity and only a slight mass decrease following 1-week incubation
in either PBS or simulated body fluid (SBF), in contrast to EDC crosslinked
collagen. Furthermore, FTIR, SEM and EDS revealed deposition of a
calcium-phosphate phase on SBF-retrieved samples, whereby an increased calcium
phosphate ratio was observed in hydrogels with higher Ph content. 72-hour
material extracts were well tolerated by L929 mouse fibroblasts, whereby cell
confluence and metabolic activity (MTS assay) were comparable to those of cells
cultured in cell culture medium (positive control). In light of their
controlled structure-function properties, these biocompatible collagen
hydrogels represent attractive material systems for potential mineralised
tissue applications.