  Electronic functionalities in materials from silicon to transition metal
oxides are to a large extent controlled by defects and their relative
arrangement. Outstanding examples are the oxides of copper, where defect order
is correlated with their high superconducting transition temperatures. The
oxygen defect order can be highly inhomogeneous, even in "optimal"
superconducting samples, which raises the question of the nature of the sample
regions where the order does not exist but which nonetheless form the "glue"
binding the ordered regions together. Here we use scanning X-ray
microdiffraction (with beam 300 nm in diameter) to show that for La2CuO4+y, the
"glue" regions contain incommensurate modulated local lattice distortions,
whose spatial extent is most pronounced for the best superconducting samples.
For an underdoped single crystal with mobile oxygen interstitials in the spacer
La2O2+y layers intercalated between the CuO2 layers, the incommensurate
modulated local lattice distortions form droplets anticorrelated with the
ordered oxygen interstitials, and whose spatial extent is most pronounced for
the best superconducting samples. In this simplest of high temperature
superconductors, there are therefore not one, but two networks of ordered
defects which can be tuned to achieve optimal superconductivity. For a given
stoichiometry, the highest transition temperature is obtained when both the
ordered oxygen and lattice defects form fractal patterns, as opposed to
appearing in isolated spots. We speculate that the relationship between
material complexity and superconducting transition temperature Tc is actually
underpinned by a fundamental relation between Tc and the distribution of
ordered defect networks supported by the materials.